Superior energy storage performance in NaNbO3‐based lead‐free ceramics under low electric field

Kun Liu,Ping Peng,Zhongqian Lv,Hengchang Nie,Genshui Wang

DOI: https://doi.org/10.1111/jace.20209

IF: 4.186

2024-10-18

Journal of the American Ceramic Society

Abstract:A new strategy for achieving excellent energy storage property of NN‐based ceramics was proposed. A modified two‐step sintering method is employed to sustain the high Pmax of BNT under low electric field. Huge Wrec of 5.10J/cm3 and high η of 85% are obtained at a low electric field of 290 kV/cm. The presence of Pnma (R) phase and Pbma (P) phase is conducive to achieve excellent properties of Wrec and η. NaNbO3 (NN)‐based materials have attracted widespread attention due to their advanced energy storage performance and eco‐friendliness. However, achieving high recoverable energy storage densities (Wrec) and efficiency (η) typically requires ultrahigh electric fields (E > 300 kV/cm), which can limit practical use. In this work, we present a synergistic strategy that employs the ferroelectric material Bi0.5Na0.5TiO3 (BNT) to augment the Pmax and the linear material Bi0.2Sr0.7TiO3 (BST) to optimize the P–E loops. Furthermore, a two‐step sintering process is implemented to preserve high Pmax values under lower electric field. As a result, ternary (1−x)(0.90NN‐0.10BNT)‐xBST was successfully prepared, achieving a high Wrec of 5.1 J/cm3 and a η of 85% in x = 0.20 samples at a low electric field of 290 kV/cm. Moreover, the x = 0.20 samples showed good frequency stability (1–200 Hz) and temperature stability (27°C–100°C). These results provide guidance for the development of ceramics with high energy storage properties under low electric fields.

materials science, ceramics