Ultra-stable dielectric properties and enhanced energy storage density of BNT-NN-based ceramics via precise core-shell structure controlling

Chaoqiong Zhu,Aoyu Li,Xinheng Li,Shiheng Li,Zunpeng Feng,Ziming Cai,Peizhong Feng,Xiaohui Wang

DOI: https://doi.org/10.1016/j.jallcom.2024.177556

IF: 6.2

2024-11-19

Journal of Alloys and Compounds

Abstract:High discharge-energy-storage-density ( W dis ) at low electric field is in high demand for advanced ceramics. In this work, a core-shell structure is well constructed and meticulously adjusted to enhance the energy storage properties. The meticulous control of the coating layer can effectively improve the breakdown strength ( E b ), ensure a high polarization, and achieve a significant optimization of temperature stability, simultaneously. Compared with 0.78Bi 0.5 Na 0.5 TiO 3 -0.22NaNbO 3 (BNTNN) ceramics without coating layer, the wt%SiO 2 ceramics achieve an inspiring improvement of 50 % in E b , which is benefit from the finer grains and the enhanced band gap. Notably, the wt%SiO 2 ceramics obtain a superior W dis of 6.17 J/cm 3 at 330 kV/cm. Importantly, wt%SiO 2 ceramics display an ultra-stable temperature stability with a high dielectric of 1350 ± 2.5 % over a wide temperature range from 35 to over 400 °C. The meticulous control of core-shell structure is expected to be a general and effective way to improve the energy-storage performance of diverse dielectric ceramics.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering