Abstract:Solid-state electrolytes are key materials for developing high-safety solid-state Li-ion batteries. The garnet-type Li7La3Zr2O12 (LLZO) solid electrolyte is one of the most promising solid electrolytes due to its high conductivity and feasible preparation in ambient air. Among several dopants, Ta-doped LLZO (Ta-LLZO) delivers high stability against lithium metal and high conductivity, which attracts lots of researchers. However, production of Ta-LLZO ceramics is less problematic due to the complicated gas–liquid–solid sintering mechanism. This work aims to develop an efficient method to produce Ta-LLZO solid electrolyte ceramic pellets, including providing a stacking sintering method and optimizing the amount of excessive Li source, the wet milling duration, and the sintering temperature. First, a low-cost, efficient “gravel-separator” strategy is provided for multiple sintering of LLZO. Second, the Li6.5La3Zr1.5Ta0.5O12 (Ta5) samples with different excessive Li levels (2, 4, 6, and 8%) are sintered at various sintering conditions of 1240 °C for 60 min, 1280 °C for 20 min, and 1320 °C for 2 min to search for the optimum excessive amount of Li. Third, Ta5 samples with optimized excessive Li (4, 6%) after milling for longer duration are sintered at 1280 °C for 30 min, 1300 °C for 10 min, 1320 °C for 10 min, 1320 °C for 30 min to finally optimize the preparation craft. After optimization, the Ta5 ceramics with excessive 4 and 6% Li sintered at 1320 °C for 10 min deliver homogeneous and dense cross-sectional morphology, high conductivity of over 1 × 10–3 S cm–1 at room temperature, and relative densities of above 96%. Furthermore, symmetric Li cells assembled with the Ta-LLZO solid electrolyte prepared with the optimized method deliver a critical current density of 1.28 mA cm–2 at 30 °C and over 1000 h of stable cycling at 0.2 mA cm–2 (0.2 mA h cm–2) at 30 °C.

Study on the role of Li2O–Ga2O3-GeO2-Gd2O3 glass doped into Li7La3Zr2O12 solid-state electrolyte

Ga-doped lithium lanthanum zirconium oxide electrolyte for solid-state Li batteries

Improvement of Ionic Conductivity in Li7La3Zr2O12 (LLZO) Solid Electrolyte By Doping with Aluminum/Tungsten

Study of Codoping Effects of Ta5+ and Ga3+ on Garnet Li7La3Zr2O12

Tri-Doping of Sol–Gel Synthesized Garnet-Type Oxide Solid-State Electrolyte

Preparation and performances of gallium-doped LLZO electrolyte with high ionic conductivity by rapid ultra-high-temperature sintering

Al-doped Li7La3Zr2O12 garnet-type solid electrolytes for solid-state Li-Ion batteries

Co-doping strategy enhanced the ionic conductivity and excellent lithium stability of garnet-type Li7La3Zr2O12 electrolyte in all solid-state lithium batteries

Crystal Structure and Preparation of Li7La3Zr2O12 (LLZO) Solid-State Electrolyte and Doping Impacts on the Conductivity: An Overview

Amorphous Phase Induced Lithium Dendrite Suppression in Glass-Ceramic Garnet-Type Solid Electrolytes

Interfacial Modification of Ga-Substituted Li 7 La 3 Zr 2 O 12 against Li Metal via a Simple Doping Method

Synergetic Effect of Li-Ion Concentration and Triple Doping on Ionic Conductivity of Li7La3Zr2O12 Solid Electrolyte

Melt-casted Li1.5Al0.3Mg0.1Ge1.6(PO4)3 glass ceramic electrolytes: A comparative study on the effect of different oxide doping

Production of Ta-Doped Li 7 La 3 Zr 2 O 12 Solid Electrolyte with High Critical Current Density

Recent Strategies for Lithium-Ion Conductivity Improvement in Li7La3Zr2O12 Solid Electrolytes

Experimental and theoretical study on enhanced electrochemistry of aluminum substitution LLZO garnet solid electrolytes

Preparation of dense Ta-LLZO/MgO composite Li-ion solid electrolyte: Sintering, microstructure, performance and the role of MgO

Comprehensive Dopant Screening in Li7La3Zr2O12 Garnet Solid Electrolyte

Enhanced Performance of Li6.4La3Zr1.4Ta0.6O12 Solid Electrolyte by the Regulation of Grain and Grain Boundary Phases.

Experimental and Computational Study of Mg and Ta‐Doped Li7La3Zr2O12 Garnet‐Type Solid Electrolytes for All‐Solid‐State Lithium Batteries