Abstract:Given the issues related to poor hydration activity, long setting time and low early strength of industrial by-product fluorogypsum (FG), the composite modifiers (Na 2 SO 4 and NaNO 2 ) were utilized to enhance its reactivity. The investigation of the mechanism involved the utilization of contemporary analytical methods, including X-ray diffraction (XRD), 1 H low-field nuclear magnetic resonance (NMR), and Scanning electron microscope and Energy Dispersive Spectrometer (SEM-EDS). The results demonstrated that the incorporation of modifiers significantly enhanced both the hydration rate and activity of fluorogypsum. The optimum concentration of the composite modifier was found to be 1.5 wt% Na 2 SO 4 and 0.5 wt% NaNO 2 . The addition of modifiers (1.5 wt% Na 2 SO 4 and 0.5 wt% NaNO 2 ) significantly shortens the setting time of FG paste, reducing it by approximately 500 min compared to the control sample. After 28 days of curing, the flexural strength and compressive strength of the fluorogypsum sample containing modifiers (1.5 wt% Na 2 SO 4 and 0.5 wt% NaNO 2 ) increased by 55.5 % (reaching 4.2 MPa) and 31.5 % (reaching 37.6 MPa), respectively. The modifiers facilitate the transformation from anhydrite (CaSO 4 , AH) to dihydrate gypsum (CaSO 4 ·2H 2 O, DH). Both NaNO 2 and Na 2 SO 4 alter the growth rates of different crystal axes during DH crystal growth, transforming them into prismatic and needle-shaped DH. The prismatic and needle-shaped DH crystals were arranged in layers, resulting in a compact structure with low hole content and few pores, which led to increased density of the hardened paste and higher strength. The current study provides evidence that the inclusion of composite modifiers greatly improves the activity of FG, making it more efficient in the field of building materials.

Role of NaF on the performances of β-hemihydrate gypsum plaster

Study on activation of fluorogypsum by sodium sulfate and sodium nitrite

Effect of soluble fluorine on the hydration, strength and microstructure of hemihydrate phosphogypsum

Reuse of Phosphogypsum As Hemihydrate Gypsum: the Negative Effect and Content Control of H3PO4

Effect of borax on the hydration and hardening of β-hemihydrate gypsum at high water–plaster ratio

Effect of sodium fluoride on the crystal regulation of high-strength α-hemihydrate gypsum from calcium sulphate dihydrate and phosphogypsum

Preparation and Performance Study of Alkali-active Gypsum Mixture System

Effect Of Potassium Sodium Tartrate And Sodium Citrate On The Preparation Of Alpha-Calcium Sulfate Hemihydrate From Flue Gas Desulfurization Gypsum In A Concentrated Electrolyte Solution

Insights into the Role of Na+ on the Transformation of Gypsum into Α-Hemihydrate Whiskers in Alcohol–Water Systems

Interaction Between Α-Calcium Sulfate Hemihydrate and Superplasticizer from the Point of Adsorption Characteristics, Hydration and Hardening Process

Effect of Fluorine and Phosphorus Impurities in Phosphogypsum on Microstructure and Mechanism of α‐Type Hemihydrate Gypsum Crystals

Performance Optimization and Characterization of Soda Residue-Fly Ash Geopolymer Paste for Goaf Backfill: Beta-Hemihydrate Gypsum Alternative to Sodium Silicate

The Influences of Soluble Phosphorus on Hydration Process and Mechanical Properties of Hemihydrate Gypsum under Deep Retarding Condition

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum

Modifications in water resistance and engineering properties of β-calcium sulphate hemihydrate plaster-superplasticizer blends

Effect of Soluble P2O5 Form on the Hydration and Hardening of Hemihydrate Phosphogypsum

Performance and Nanostructure Simulation of Phosphogypsum Modified by Sodium Carbonate and Alum

Preparing sulfoaluminate cement using phosphogypsum as the only calcium oxide source: Effects of fluoride impurities

Research on formulation optimization and hydration mechanism of phosphogypsum-based filling cementitious materials