Abstract:The research was mainly focused on the phase transformation of Ti-42Al-5Mn (at%) alloy produced by vacuum induction melting (VIM) and vacuum arc remelting (VAR) followed by wrought process. The phase transformation kinetics of the alloy during continuous cooling under the cooling rates of 0.1 degrees C/s, 0.5 degrees C/s, 2 degrees C/s, 10 degrees C/ s, 50 degrees C/s, and 200 degrees C/s were identified by the Gleeble-3800 system, which is finally used to construct a schematic continuous cooling transformation (CCT) diagram of this alloy. The related phase composition, microstructure and property of the alloy were studied using X-ray diffraction (XRD), electron probe micro analyzer (EPMA), transmission electron microscope (TEM) and Vickers hardness (HV). It shows that six kinds of phase transformation are existed during continuous cooling from 1300 degrees C with the cooling rates of 0.1 degrees C/s, 0.5 degrees C/s, 2 degrees C/s, 10 degrees C/s, 50 degrees C/s, 200 degrees C/s and WQ, including beta ->alpha(2)', beta ->alpha, beta ->gamma, beta ->beta(o)/alpha ->alpha(2), alpha(2)->alpha(2)/gamma and alpha(2)/gamma ->beta(o,sec).It reveals that partial transformations would be inhibited when the cooling rate is relatively high. The martensitic structures (alpha(2)') obtained by beta ->alpha(2) were formed under the WQ condition after holding at 1300 degrees C for 5min, and it will be completely restrained below the cooling rate of WQ. For the beta ->gamma, it is restrained if the cooling rates are higher than 50 degrees C/s. The alpha(2)->alpha(2)/gamma could be also suppressed when cooling with 200 degrees C/s, and the gamma lath within the supersaturated alpha(2)-grains would be formed at lower cooling rate below 50 degrees C/s. For 0.5 degrees C/s and 0.1 degrees C/s, a small amount of dotted beta(o) (beta(o,sec)) phases can be formed in the lamellar interfaces, which is proved the reaction products of alpha(2)/gamma ->beta(o,sec). Furthermore, the effect of cooling rates on the microstructure, including interlamellar spacing (lambda) and gamma grains are also identified and discussed.

Phase Transformations in Cd0.96Mn0.04Te0.98Se0.02 Solid Solutions

Mid-temperature Thermoelectric Performance of Zone-Melted Sb2(Te,Se)3 Alloys Near Phase Transition Boundary

Structural and Magnetic Phase Transitions in MnTe-MnSe solid solutions

Phase Transformation Behavior of a Β-Solidifying Γ-Tial-based Alloy from Different Phase Regions with Various Cooling Methods

Phase Diagram of the System Tl2Te–Tl5Te3–Tl9GdTe6

Phase separation of a supersaturated nanocrystalline Cu Co alloy and its influence on thermal stability

Phase Transformation Behavior of a Mn Containing Β-Solidifying Γ-Tial Alloy During Continuous Cooling

Phase Equilibria of the Cu-Se-Te Ternary System

Phase Equilibria in the Ag2Te-PbTe-Sb2Te3 System and Thermodynamic Properties of the (2PbTe)1-x(AgSbTe2)x Solid Solutions

Microstructure Evolution of the Phase Change Material Tisbte

Phases Formation and Evolution at Elevated Temperatures of Al–12Si–3.8Cu–2Ni–1Mg Alloy†

PHASE EQUILIBRIA IN THE SECTION Cu2Se – Cu3SbSe4

Phase Transformation Of Beta-Fesi2-Based Alloys Under In-Situ High-Temperature And High-Pressure X-Ray Diffraction Measurements

Experimental Investigation of Phase Equilibria in the Co-Ta-Si Ternary System

Differential Scanning Calorimetry Study on Transformations in A Ni47ti50fe3 Alloy

The Cu–Te system: Phase relations determination and thermodynamic assessment

Liquidus Projection and Phase Equilibria Isothermal Section of Se–Sn–Te System

Melting and Vaporization of the 1223 Phase in the System (Tl-Pb-Ba-Sr-Ca-Cu-O)

Phase transformation of /spl beta/-FeSi/sub 2/-based alloys under in-situ high-temperature and high-pressure X-ray diffraction measurements

Phase Relations in the Tl2Te-TlBiTe2-TlGdTe2 Compositions Region of the Tl-Bi-Gd-Te System and Magnetic Properties of the TlBi1−xGdxTe2 Solid Solutions

Influence of W, Mo and Ti trace elements on the phase separation in Al8Co17Cr17Cu8Fe17Ni33 based high entropy alloy