Abstract:Additive manufacturing (AM) refers to advanced technologies for building 3D objects by adding material layer upon layer using either electron beam melting (EBM) or selective laser melting. AM allows us to produce lighter and more complex parts. However, various defects are created during the AM process, which severely affect fatigue behavior. In the current research, the effects of the anisotropic microstructure in the in-plane and out-of-plane orientations and defects on the fatigue crack propagation rate (FCPR) and crack path were studied. A resonance machine was used to determine the fatigue crack propagation rate (da/dN vs. ΔK) from the near-threshold up to the final fracture, accompanied by in situ Acoustic Emission (AE) monitoring. Micro-Computerized Tomography (μCT) enabled us to characterize surface and microstructural defects. Metallography was used to determine the microstructure vs. orientations and fractography to classify the fatigue fracture propagation modes. Calculations of the local stress distribution were performed to determine the interactions of the cracks with the defects. In the out-of-plane direction, the material exhibited high fatigue fracture toughness accompanied by a slightly lower fatigue crack propagation rate as compared to in-plane orientations. The near-threshold stress intensity factor was slightly higher in the out-of-plane orientation as compared to that in the in-plane one, accompanied by a lower exponent of the Paris law regime. The threshold decreased with an increasing load ratio as expected for both orientations. The crack propagation direction that crosses the elongated grains plays an important role in increasing fatigue resistance in the out-of-plane direction. In the in-plane directions, the crack propagates parallel to the grain boundary, interacts with more defects and exhibits more brittle striations on the fracture surface, resulting in lower fatigue resistance.

Short Crack Behavior of an Additively Manufactured Ti–6Al–4V Alloy Under Ultrasonic High Cycle Fatigue Testing

Characteristic and mechanism of crack initiation and early growth of an additively manufactured Ti-6Al-4V in very high cycle fatigue regime

Modelling the Variability and the Anisotropic Behaviour of Crack Growth in SLM Ti-6Al-4V

Effects of Anisotropic Microstructure and Load Ratio on Fatigue Crack Propagation Rate in Additively Manufactured Ti-6Al-4V Alloy

Crack Initiation Mechanism in a High-Strength Ti-5Al-7.5V Alloy Subjected to High Cycle Fatigue Loading

The Role of Microstructure and Local Crystallographic Orientation Near Porosity Defects on the High Cycle Fatigue Life of an Additive Manufactured Ti-6Al-4V

Evaluation of Fatigue Behaviors of SLMed Ti-6Al-4V in High-Cycle and Very-High-Cycle Regimes Considering Effects of Stress Ratio and Surface Roughness

Fatigue Crack Growth Rates and Crack Tip Opening Loads in CT Specimens Made of SDSS and Manufactured Using WAAM

Fatigue crack growth behavior in an aluminum alloy Al–Mg–0.3Sc produced by wire based directed energy deposition process

Fatigue Crack Segmentation and Characterization of Additively Manufactured Ti‐6Al‐4V Using X‐Ray Computed Tomography

Fatigue Crack-Initiation Mechanisms of a Dual-Phase Titanium Alloy Exhibiting High Tensile and High-Cycle Fatigue Properties

Cyclic Deformation and Microcrack Initiation During Stress Controlled High Cycle Fatigue of a Titanium Alloy

Crack Initiation Mechanisms under Two Stress Ratios Up to Very-High-cycle Fatigue Regime for a Selective Laser Melted Ti-6Al-4V

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Surface Treatment of Powder-Bed Fusion Additive Manufactured Metals for Improved Fatigue Life

Fatigue Crack Initiation and Growth Behaviors of Additively Manufactured Ti-6AI-4V Alloy After Hot Isostatic Pressing Post-Process

High‐cycle and Very‐high‐cycle Fatigue Behavior at Two Stress Ratios of Ti‐6Al‐4V Manufactured Via Laser Powder Bed Fusion with Different Surface States

In situ X-ray imaging of fatigue crack growth from multiple defects in additively manufactured AlSi10Mg alloy

Multi-scale Study of Subsurface Fatigue Cracking Behavior of Laser-Powder Bed Fused Inconel 718 at Stress Ratios and Temperatures

X-ray imaging of defect population and the effect on high cycle fatigue life of laser additive manufactured Ti6Al4V alloys

An experimental investigation of fatigue performance and crack initiation characteristics for an SLMed Ti-6Al-4V under different stress ratios up to very-high-cycle regime