Abstract:<p>The effect of adding of 0.13 wt. % Cr on the primary recrystallization and magnetic properties of high permeability grain oriented silicon steel was studied. The results show that trace Cr refined both primary and secondary grains. The reduction of final grain size resulted in decrease of 5.1%, 4.0% and 3.6% in the average of iron loss during magnetization at 50Hz, 100 Hz and 200 Hz, respectively. Besides the conventional precipitates, there were two kinds of Cr-containing nitrides, i.e., the amorphous (Si, Cr) N formed in the matrix, and the crystalline fcc-CrN formed at grain boundary. These precipitates acted as inhibitors to refine and homogenize primary grains in the thickness direction. The beneficial {111}<112> texture component increased, while the components that cannot form high-energy grain boundaries with Goss grains, such as {001}<110> and {112}<110> at different thickness layers decreased after primary recrystallization.</p>
What problem does this paper attempt to address?
The paper attempts to address the issue of improving the primary recrystallization characteristics and magnetic properties of high magnetic permeability oriented silicon steel by adding trace amounts of chromium (Cr). Specifically, the study investigates the effect of adding 0.13 wt% Cr on the grain refinement and magnetic properties of high magnetic permeability oriented silicon steel during low-temperature reheating. The main objective of the paper is to explore how the addition of Cr affects the microstructure and magnetic properties of the material, particularly iron loss and magnetic induction.
### Research Background
The energy consumption of transformers is mainly composed of iron loss in the core and copper loss in the coils, where the magnetic properties of the core material directly affect the iron loss and energy efficiency of the transformer. Therefore, manufacturers have been striving to develop oriented silicon steel with excellent magnetic properties to meet the requirements of high-efficiency transformers. High magnetic permeability and low iron loss are important characteristics of oriented silicon steel. However, further improving magnetic induction has become very difficult, so researchers and manufacturers have been exploring techniques to reduce iron loss by optimizing grain size, texture, and morphology.
### Research Objectives
This study aims to investigate the effect of adding 0.13 wt% Cr on the primary recrystallization characteristics and magnetic properties of high magnetic permeability oriented silicon steel during low-temperature reheating. The specific objectives include:
1. **Grain Refinement**: To study how the addition of Cr affects the refinement of primary recrystallization grains.
2. **Magnetic Performance Improvement**: To evaluate the impact of Cr addition on iron loss and magnetic induction.
3. **Microstructure Analysis**: To analyze the effect of Cr addition on the type and distribution of precipitates using transmission electron microscopy (TEM) and other methods.
### Main Findings
1. **Reduction in Iron Loss**: After adding 0.13 wt% Cr, iron loss decreased by 5.1%, 4.0%, and 3.6% at frequencies of 50 Hz, 100 Hz, and 200 Hz, respectively.
2. **Grain Refinement**: The addition of Cr refined the primary recrystallization grains, reducing the average size of the final grains.
3. **Changes in Precipitates**: Two types of Cr-containing nitrides were formed, namely amorphous (Si, Cr)N in the matrix and crystalline fcc-CrN at the grain boundaries. These precipitates acted as inhibitors, helping to refine and homogenize the primary recrystallization grains.
4. **Texture Changes**: Beneficial {111}〈112〉 texture components increased, while {001}〈110〉 and {112}〈110〉 texture components, which cannot form high-energy grain boundaries with Goss grains, decreased.
### Conclusion
By adding 0.13 wt% Cr, the primary recrystallization process can be effectively controlled, grain refinement can be achieved, and texture can be improved, thereby significantly reducing iron loss. Although magnetic induction slightly decreased, the overall magnetic performance of the material was enhanced. These results provide important references for the development of high-performance oriented silicon steel.