An efficient graphene oxide reinforced aluminum phosphate/Cr2O3 double coating as an enhanced tritium permeation barrier
Wei Liu,Lihong Xue,Jiao Di,Qilai Zhou,Hang Zhang,Heping Li,Youwei Yan
DOI: https://doi.org/10.1016/j.surfcoat.2020.126699
IF: 4.865
2021-01-01
Surface and Coatings Technology
Abstract:<p>Fabrication of dense ceramic coating on steels is one of the most efficient methods to prevent hydrogen ingress into the structural materials. In this study, a dense graphene oxide (GO)-reinforced AlPO<sub>4</sub> composite layer on a Cr<sub>2</sub>O<sub>3</sub> coating was successfully fabricated by the dip coating method. The effects of GO content on the microstructure, phase compositions, mechanical and hydrogen isotope barrier properties were investigated. The results show that GO can effectively improve the mechanical properties of the double-coated specimens and the GO-reinforced AlPO<sub>4</sub> composite layer has a positive effect on the improvement of deuterium permeation resistance. The 0.050 GO-AlPO<sub>4</sub>/Cr<sub>2</sub>O<sub>3</sub> sample with a dense and uniform double-coating structure demonstrates the best overall performance. The microhardness, bonding strength, corrosion voltage, and corrosion current can reach 317.3 HV, 21.5 MPa, −77 mV, and 3.92 × 10<sup>−9</sup> A·cm<sup>−2</sup>, respectively. In addition, the deuterium permeability reduction factor (PRF) in the temperature range of 450–550 °C is greatly improved. This enhancement can be attributed to the chemical inertness and barrier effect of GO and the synergy effects of GO-reinforced AlPO<sub>4</sub> layer and Cr<sub>2</sub>O<sub>3</sub> layer. As the test temperature rises to 600 °C, the phase transition of Cr<sub>2</sub>O<sub>3</sub> is observed, and the phase transition process is revealed by thermodynamic method.</p>
physics, applied,materials science, coatings & films