Abstract:A new three-step method for preparing aluminum rich coating on HR-2 stainless steel was proposed, i.e. ambient temperature chloroaluminate melts electroplating followed by heat treating and artificial oxidation. In the electroplating process, aluminum deposition from AlCl3/MEIC to the surface of HR-2 steel was performed with a deposition rate of 15 mu m/h. Within the aluminizing temperature range from 650 to 750 degrees C, aluminizing time from 1 to 30 h, the aluminized coating with thickness of 3-27 mu m can be prepared, which is homogeneous and free of porosity or crack, and have good metallographic adherence to the substrate; the coating cross section exhibits a three-layer or two-layer structure. A simple Arrhenius relationship can be used to describe the effect of temperature on the coating growth rate, which gives activation energy of 116.9 kJ/mol. The relationship between the coating thickness against time(1/2) is approximately linear, which is a typical feature of the diffusion controlled coating growth mechanism. To form Al2O3 film on surface, the aluminized coating treated for 4 h was oxidized in 10(-2) Pa O-2 for 80 h and observed by X-ray photoelectron spectroscopy (XPS) and Reflection spectrum. The finally fabricated coating shows a double-layer structure consisting of an outer gamma-Al2O3 layer with thickness of 110 nm and inner (Fe,Cr,Mn and Ni)Al/(Fe,Cr,Mn and Ni)(3)Al layer of 30 mu m thickness, and is homogeneous without any defects. The deuterium permeation rate through the coated HR-2 steel is reduced by 3 orders of magnitude at 600 degrees C. The coating remains a perfect surface for 20 thermal cycles between 750 degrees C and room temperature. The method is a potential candidate for preparation of TPB on the tritium container surface in ITER.

Design and Properties of FeAl/Al2O3/TiO2 Composite Tritium-Resistant Coating Prepared Through Pack Cementation and Sol–gel Method

A new preparing method and performances of FeAl/Al2O3 tritium permeation barrier

Preparation and Properties of FeAl/Al2O3 Composite Tritium Permeation Barrier Coating on Surface of 316L Stainless Steel

Tritium Permeation Barrier-Aluminized Coating Prepared by Al-Plating and Subsequent Oxidation Process

Preparation and Properties of Al2O3/SiO2 Composite Tritium Permeation Barrier and Its Effects on the Inner Walls of Pipelines

Sol–gel prepared Al2O3 coatings for the application as tritium permeation barrier

Enhancing Disproportionation Resistance of Zr2Co-based Alloys by Regulating the Binding Energy of H Atom

A dense Fe-Al/Al2O3 coating as tritium permeation barrier on CLAM steel by hot-dipping aluminizing

Preparation and Hydrogen Penetration Performance of TiO2/TiCx Composite Coatings

Hydrogen Permeation Properties of CrxCy@Cr2O3/Al2O3 Composite Coating Derived from Selective Oxidation of a CrC Alloy and Atomic Layer Deposition

One-step preparation of α-Al2O3/SiO2 composite tritium permeation barrier via slurry spin coating method and performance investigation

A Study on the Radiation Resistance Performance of an Al2O3 Composite Tritium Permeation Barrier and Zirconium-Based Tritium-Absorbing Materials

Thermochemically synthesized α‐Al2O3 composite coating with high bonding strength and deuterium permeation resistance

Hydrogen Interaction Characteristics of a Cr2O3Y2O3 Coating Formed on Stainless Steel in an Ultra-Low Oxygen Environment

Effect of Mechanical Damage on Tritium Permeability Resistance of FeAl/Al2O3 Coating on 316L Stainless Steel

Preparation and Hydrogen Barrier Property of FexAly/Al/Al2O3 Composite Coating on X80 Steel Surface

Preparation of Al-Cr-Fe Coatings by Heat Treatment of Electrodeposited Cr/Al Composite Coatings

An efficient graphene oxide reinforced aluminum phosphate/Cr2O3 double coating as an enhanced tritium permeation barrier

An Al 2 O 3 /Ni–Al tritium permeation barrier coating for the potential application in thorium-based molten salt reactor

Preparation and Characterization of SiO<sub>2</sub>/-Al<sub>2</sub>O<sub>3</sub> Tritium Permeation Barriers at Low Temperature

Study on Preparation and Performance of ZrCo/Ti Tritium Storage Composite Film