Abstract:A new three-step method for preparing aluminum rich coating on HR-2 stainless steel was proposed, i.e. ambient temperature chloroaluminate melts electroplating followed by heat treating and artificial oxidation. In the electroplating process, aluminum deposition from AlCl3/MEIC to the surface of HR-2 steel was performed with a deposition rate of 15 mu m/h. Within the aluminizing temperature range from 650 to 750 degrees C, aluminizing time from 1 to 30 h, the aluminized coating with thickness of 3-27 mu m can be prepared, which is homogeneous and free of porosity or crack, and have good metallographic adherence to the substrate; the coating cross section exhibits a three-layer or two-layer structure. A simple Arrhenius relationship can be used to describe the effect of temperature on the coating growth rate, which gives activation energy of 116.9 kJ/mol. The relationship between the coating thickness against time(1/2) is approximately linear, which is a typical feature of the diffusion controlled coating growth mechanism. To form Al2O3 film on surface, the aluminized coating treated for 4 h was oxidized in 10(-2) Pa O-2 for 80 h and observed by X-ray photoelectron spectroscopy (XPS) and Reflection spectrum. The finally fabricated coating shows a double-layer structure consisting of an outer gamma-Al2O3 layer with thickness of 110 nm and inner (Fe,Cr,Mn and Ni)Al/(Fe,Cr,Mn and Ni)(3)Al layer of 30 mu m thickness, and is homogeneous without any defects. The deuterium permeation rate through the coated HR-2 steel is reduced by 3 orders of magnitude at 600 degrees C. The coating remains a perfect surface for 20 thermal cycles between 750 degrees C and room temperature. The method is a potential candidate for preparation of TPB on the tritium container surface in ITER.

One-step preparation of α-Al2O3/SiO2 composite tritium permeation barrier via slurry spin coating method and performance investigation

A new preparing method and performances of FeAl/Al2O3 tritium permeation barrier

Preparation and Properties of Al2O3/SiO2 Composite Tritium Permeation Barrier and Its Effects on the Inner Walls of Pipelines

Tritium Permeation Barrier-Aluminized Coating Prepared by Al-Plating and Subsequent Oxidation Process

Preparation and Properties of FeAl/Al2O3 Composite Tritium Permeation Barrier Coating on Surface of 316L Stainless Steel

Preparation and Characterization of SiO<sub>2</sub>/-Al<sub>2</sub>O<sub>3</sub> Tritium Permeation Barriers at Low Temperature

Design and Properties of FeAl/Al2O3/TiO2 Composite Tritium-Resistant Coating Prepared Through Pack Cementation and Sol–gel Method

An Al 2 O 3 /Ni–Al tritium permeation barrier coating for the potential application in thorium-based molten salt reactor

Preparation of α-Al2O3/NiAl multilayer coatings on GH3535 superalloy surface by pack cementation and subsequent in-situ oxidation

Al-Cr Coatings Prepared by Diffusion at Low Temperature and Its Phase Characterization

A dense Fe-Al/Al2O3 coating as tritium permeation barrier on CLAM steel by hot-dipping aluminizing

Simulation of the effects of different substrates, temperature, and substrate roughness on the mechanical properties of Al2O3 coating as tritium penetration barrier

Comparative study on the effects of α/γ phase ratio on the micro-structures and properties in Al2O3 coatings under silicon ion irradiation

Effects of Heat Treatment on Structure Transformation of Cr/Al Composite Coatings

Preparation of -Al<sub>2</sub>O<sub>3</sub>/NiAl multilayer coatings on GH3535 superalloy surface by pack cementation and subsequent in-situ oxidation

A Study on the Radiation Resistance Performance of an Al2O3 Composite Tritium Permeation Barrier and Zirconium-Based Tritium-Absorbing Materials

Preparation and Hydrogen Penetration Performance of TiO2/TiCx Composite Coatings

Microstructure and properties evolution of plasma sprayed Al2O3-Y2O3 composite coatings during high temperature and thermal shock treatment

Chemical compatibility between the α-Al2O3 tritium permeation barrier and Li4SiO4 tritium breeder

Preparation of SiC Composite Coating on the Surface of Graphite Spheres in VHTR

Thermochemically synthesized α‐Al2O3 composite coating with high bonding strength and deuterium permeation resistance