Bismuth vanadate photoanode synthesized by electron-beam evaporation of a single precursor source for enhanced solar water-splitting
Sung Won Hwang,Dong Hyun Seo,Jin Un Kim,Dong Kyu Lee,Kyoung Soon Choi,Cheolho Jeon,Hak Ki Yu,In Sun Cho
DOI: https://doi.org/10.1016/j.apsusc.2020.146906
IF: 6.7
2020-10-01
Applied Surface Science
Abstract:Bismuth vanadate (BiVO4, BVO) is a promising photoanode material for photoelectrochemical water-splitting, and it is mostly prepared using a sol-gel spin-coating method. BVO often exhibits poor PEC performance without modifications such as doping, co-catalyst deposition, and heterojunction formation. Herein, we report an alternative method to deposit a phase-pure BVO film using the electron-beam evaporation (EB) method. Specifically, electron-beam irradiation on the BVO source generates BVO precursor vapors, depositing an amorphous BVO film. The substrate temperature and emission current (of the electron-beam) were varied to control the phase-purity and grain size of the BVO film. The surface chemical state, optical, and electrochemical properties of the BVO films were characterized using X-ray photoelectron spectroscopy, ultraviolet–visible (UV–Vis) spectroscopy, and electrochemical impedance spectroscopy measurements, respectively. Interestingly, we found that BVO prepared under optimal condition has large grains (~400 nm in lateral size) and oxygen vacancies, thus exhibiting enhanced PEC performance. The photocurrent density of ~1.0 mA/cm2 at 1.23 V versus a reversible hydrogen electrode was obtained, which is 50% higher than the sol-gel derived BVO. The photocurrent density increased further to 2.4 mA/cm2 via CoOx co-catalyst deposition. More importantly, the photocurrent stability of EB-BVO was much higher than the sol-gel BVO.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films