Sm-doped Gd2Zr2O7 thermal barrier coatings: Thermal expansion coefficient, structure and failure

Zheng Liu,Zaoyu Shen,Guanxi Liu,Limin He,Rende Mu,Zhenhua Xu

DOI: https://doi.org/10.1016/j.vacuum.2021.110314

IF: 4

2021-08-01

Vacuum

Abstract:The Gd2Zr2O7 ceramic material is a promising candidate for thermal barrier coatings. In this work, Sm-doped Gd2Zr2O7 coating was deposited by electron beam-physical vapor deposition. The Sm-doped Gd2Zr2O7 coating exhibits high thermal expansion coefficient and thermal shock lifetime at 1100 °C. The thickness of TGO layer is about 15 μm at the end. It was found that the spallation of coatings resulted from the cracks coalescence. The TGO broken played a dominant role in the failure process of the Sm-doped Gd2Zr2O7 coating.

materials science, multidisciplinary,physics, applied

What problem does this paper attempt to address?

The paper mainly focuses on the application of samarium-doped gadolinium zirconate (Sm-doped Gd2Zr2O7) as a potential thermal barrier coating material, particularly in comparison to traditional yttria-stabilized zirconia (YSZ) thermal barrier coatings, in terms of its thermal expansion coefficient (TEC) and thermal shock lifetime performance. The paper prepared samarium-doped gadolinium zirconate coatings using electron beam physical vapor deposition (EB-PVD) technology and explored their microstructure, thermal expansion coefficient, and failure mechanisms under high-temperature conditions.

Specifically, the study found that the samarium-doped gadolinium zirconate coating has a higher thermal expansion coefficient (11.22 × 10^(-6)/K) and a longer thermal shock lifetime (6735 cycles). These excellent properties are mainly attributed to the enhanced structural stability brought by samarium doping, the increased thermal expansion coefficient, and the presence of a feather-like nanostructure. Additionally, the paper analyzed the impact of the thermal barrier oxide (TGO) layer thickness on the coating's failure, pointing out that when the TGO layer thickness reaches approximately 15 micrometers, the coating begins to crack and eventually leads to spallation. Therefore, the research results indicate that samarium-doped gadolinium zirconate coatings have the potential to become a new material to replace traditional YSZ coatings.