Interlaminar fracture toughness of carbon/epoxy composites laminates toughened by short carbon fiber
Yongan Wang,Wei Shen,Lifeng Chen,Lvtao Zhu,Toshiaki Natsuki
DOI: https://doi.org/10.1002/pc.27488
IF: 5.2
2023-06-09
Polymer Composites
Abstract:Short carbon fiber (SCF) interlaminar toughened carbon fiber reinforced epoxy resin (CF/EP) composite laminates were prepared by hot press process, the compiled UD prepreg was placed between two metal plates and then put into the hot press machine. Laminates were cut to specific sizes for end notched three‐point flexural (ENF), and the values of the peak load and GIIC are studied. The peak load and GIIC have the same trend, both increasing and then decreasing with increasing fiber content, with a maximum value at 10 g/m2 of short fiber content. To investigate the toughening mechanism of SCF interlaminar toughened CF/EP composites, we used SEM to observe the interlaminar fracture surfaces of the composites and analyzed the mechanism of short fiber interlaminar toughening. In this paper, short carbon fiber (SCF) interlaminar toughened carbon fiber reinforced epoxy resin (CF/EP) composite laminates were prepared. The effect of SCF content on the mode II interlaminar fracture toughness (GIIC) and flexural properties of CF/EP composites was investigated. It was shown that the addition of SCF between the plies had an effect on the GIIC of the composites. When the SCF content was 10 g/m2, the GIIC increased from 1506.62 J/m2 to 1995.6 J/m2, which improved by about 32.46%. When the content of SCF was 5 g/m2, the flexural strength and flexural modulus increased by 36.92% and 98.48%, respectively, showing the best performance. The toughening mechanism of SCF was observed by SEM images as SCF debonding and pulling out from the resin and SCF fracture. The present study was also compared with our previous study on short aramid fiber interlaminar toughened CF/EP composites, and the test data and SEM images of the two experiments were compared to analyze the effect of different short fibers on the interlaminar toughening effect, which provides some reference for the selection of interlaminar toughening materials.
materials science, composites,polymer science