Enhancement of interlaminar fracture toughness and damage mechanisms analysis in cfrps reinforced with sprayed nano particles
Huiyong He,Xin Liu,Zhanjun Wu
2017-01-01
Abstract:Three kinds of nano particles were synthesized and prepared, including nano boehmite (AlOOH)、 nano and nano montmorillonite. The purity, morphology and size of these nano particles were investigated by the methods of FTIR, XRD, SEM, and TEM, respectively. Instead of dispersing nano particles into epoxy resin, then compounding epoxy resin and carbon fibre, in this paper, those nano particles were sprayed evenly on the surface of every prepregs to enhance interlinear fracture toughness(ILFT) of the laminates, which could improve delamination resistance. In this way, difficulties in dispersing nano particles can be avoided, also, this method need not to change curing process. For comparison, baseline samples with neat prepregs were also prepared. Three groups of carbon fiber reinforced polymers (CFRPs) were fabricated. To verify nano particles sprayed between lamina can toughen CFRPs, and to analyse damage mechanisms, The end-notched flexure (ENF) test was taken at room temperature (RT, 293k) and at low temperature (LT, 77k). Low temperature environments were achieved by immersing the loading apparatus and specimen in liquid nitrogen (77 K). The fracture surfaces were examined by SEM. The results indicated that three kinds of nano particles were pure crystalline and high purity. There were obvious difference on morphology, nano boehmite (AlOOH) was needle-like and sheet, nano was cubic, and nano montmorillonite was lamellar. The ENF test results showed that ILFT of unidirectional CFRPs increased significantly when sprayed nano particles at RT, and at 1wt%, CFRPs sprayed with nano boehmite (AlOOH)、nano montmorillonite achieved max fracture toughness, 931 , increased by 29.3%, and 870 , increased by 20.8%, compared to that of the CFRPs without nano particles, respectively. But At LT, enchancing CFRPs with sprayed nano particles is not so efficient, because cryogenic toughening mechanisms are different significantly from that at RT.