Development of Low-Carbon Sea Sand Engineered Cementitious Composites (lseccs): Performance, Cracking Behavior and Trilinear Tensile Constitutive Model
Qiyao Yao,Qingbin Li,Xiaodan Teng,Danni Luo
DOI: https://doi.org/10.1016/j.conbuildmat.2024.138344
IF: 7.4
2024-01-01
Construction and Building Materials
Abstract:This study developed a sustainable low-carbon sea sand engineered cementitious composites (LSECCs). The effect of FA/GGBS weight ratios (1, 0.5, 0), W/B ratios (0.16, 0.18, 0.20, 0.25) and PE fiber vol% (2 %, 1.8 %, 1.6 %) on the tensile and compressive properties of LSECCs was investigated. The formation mechanism of its high ductility was analyzed through fracture energy, single-crack testing, and SEM images. The results show that the compressive strength of LSECCs ranges from 60.0 MPa to 88.4 MPa, the ultimate tensile strength from 6.16 MPa to 8.38 MPa, and the ultimate tensile strain from 4.27 % to 8.49 %. Decreasing the FA/GGBS weight ratio, especially to 0.5, contributes to higher compressive strength, first-crack strength, and ultimate tensile strength of LSECCs, but reduces the ductility, while increasing the average crack width and crack spacing. Increasing the W/ B ratio enhances the ductility and crack width control ability of LSECCs. The optimal volume fraction of PE fibers is 1.8 %, at which the tensile failure process of LSECCs can be divided into three stages: linear elastic, hardening, and softening with considerable load-carrying capacity. Therefore, a trilinear tensile constitutive model is proposed to more accurately describe their tensile stress-strain relationship. This model is applicable not only to LSECCs with three-stage failure characteristics but also to ECCs with two-stage (elastic and strain hardening) failure characteristics. The findings of this study can provide experimental and theoretical references for the future design and application of sustainable low-carbon engineered cementitious composites.