Boosting the Efficiency of NiO x -Based Perovskite Light-Emitting Diodes by Interface Engineering

Haoran Wang,Hao Yuan,Jiahao Yu,Chen Zhang,Kang Li,Mengqing You,Wenqiang Li,Jian Shao,Jun Wei,Xiaoyu Zhang,Rui Chen,Xuyong Yang,Weiwei Zhao

DOI: https://doi.org/10.1021/acsami.0c16139

2020-11-12

Abstract:Nickel oxide (NiO_<i>x</i>) is a promising hole-transporting material for perovskite light-emitting diodes (PeLEDs) because of its low cost, excellent stability, and simple fabrication process. However, the electroluminescence efficiencies of NiO_<i>x</i>-based PeLEDs are greatly limited by inefficient hole injection and exciton quenching at the NiO_<i>x</i>–perovskite interfaces. Here, a novel interfacial engineering method with sodium dodecyl sulfate-oxygen plasma (SDS-OP) is demonstrated to simultaneously overcome the aforementioned issues. Experimental results reveal that a short OP treatment on the top of the SDS-coated NiO_<i>x</i> significantly deepens the NiO_<i>x</i> work function (from 4.23 to 4.85 eV) because of the formation of a large surface dipole, allowing for efficient hole injection. Moreover, the SDS-OP layer passivates the electronic surface trap states of perovskite films and suppresses the exciton quenching by NiO_<i>x</i>. These improvements inhibit the nonradiative decays at the NiO_<i>x</i>–perovskite interface. As a result, the external quantum efficiency of CsPbBr₃ LEDs is increased from 0.052 to 2.5%; that of FAPbBr₃ nanocrystals LEDs is increased from 5.6 to 7.6%.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c16139?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c16139</a>.Elemental maps of the NiO_<i>x</i>/SDS-OP film, water CA of SDS-coated NiO_x, water CA of SDS-coated NiO_x treated with OP, C 1s XPS spectra of the SDS thin films treated with OP, XPS spectra of the NiO_x-OP/SDS films for Ni 2p, molecular dipole moment-induced change of the work function of the NiO_x film, Tauc plots, UPS spectra of the perovskite film, AFM images of NiOx-OP and NiOx/SDS-OP, steady-state PL spectra of quartz/perovskite and quartz/NiOx-OP/perovskite, J-V characteristics, operating lifetimes of the PeLEDs, energy levels of the perovskite films, summary of TA spectral fitting parameters, and summary of PL lifetime fitting parameters (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c16139/suppl_file/am0c16139_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology