Abstract:TiAlVN coatings gain extensive attention due to the self-lubrication effect with elevated temperatures. However, the poor oxidation resistance of TiAlVN limits their industrial application. In order to improve the oxidation resistance of TiAlVN, the TiAlSiN insertion layer is introduced into TiAlVN to synthesize nano-multilayered Ti0.40Al0.50V0.10N/Ti0.56Al0.34Si0.10N (ML_1) and Ti0.40Al0.50V0.10N/Ti0.46Al0.45Si0.09N (ML_2). Ab initio calculations combined with experiments prove that Si-doping reduces the solid solubility of Al in the cubic structure, while V-addition increases its solubility. The hardness of Ti0.40Al0.50V0.10N and Ti0.56Al0.34Si0.10N with cubic structure are 29.2 +/- 0.9 and 36.5 +/- 0.9 GPa, while Ti0.46Al0.45Si0.09N with mixed cubic and hexagonal structure exhibits low hardness of 29.1 +/- 0.9 GPa. The coherently interfacial strengthen enhances the hardness to 33.6 +/- 1.0 GPa of ML_1 and 35.2 +/- 1.1 GPa of ML_2. Additionally, the Si-containing insertion layers improve the thermal stability of TiAlVN coating, where the onset temperature of w-AlN formation during annealing is increased by similar to 200-300 degrees C. After annealing at 1200 degrees C, Ti0.40Al0.50V0.10N, Ti0.56Al0.34Si0.10N and Ti0.46Al0.45Si0.09N possess the hardness values of 26.2 +/- 1.5, 38.8 +/- 0.8 and 29.5 +/- 1.0 GPa, while ML_1 and ML_2 still manifest superior hardness values of 35.4 +/- 1.1 and 35.1 +/- 1.1 GPa. Furthermore, the oxidation resistance of our multilayers lies between that of TiAlVN and TiAlSiN. After oxidation at 700 degrees C for 10 h, Ti0.56Al0.34Si0.10N, Ti0.46Al0.45Si0.09N, ML_1 and ML_2 present oxide layers of similar to 0.1, similar to 0.1, similar to 2.3 and similar to 1.7 mu m, respectively, while Ti0.40Al0.50V0.10N coatings has been completely oxidized. (C) 2021 Elsevier B.V. All rights reserved.

Thermostability, oxidation, and high-temperature tribological properties of nano-multilayered AlCrSiN/VN coatings

The Synergy of V and Si on the Microstructure, Tribological and Oxidation Properties of AlCrN Based Coatings

The Microstructural, Mechanical and Thermal Properties of TiAlVN, TiAlSiN Monolithic and TiAlVN/TiAlSiN Multilayered Coatings

Microstructure, Mechanical, Tribological, and Oxidizing Properties of AlCrSiN/AlCrVN/AlCrNbN Multilayer Coatings with Different Modulated Thicknesses

Mechanical, oxidation, and cutting properties of AlCrN/AlTiSiN nano-multilayer coatings

Structure and Property Optimization of Ni-containing AlCrSiN Coatings by Nano-Multilayer Construction

Improving high-temperature wear resistance of arc-evaporated AlCrN coatings by Mo alloying

Insights into the oxidation resistance mechanism and tribological behaviors of multilayered TiSiN/CrVxN hard coatings

On the high temperature oxidation behavior of AlCrBN/TiAlNbSiN multilayer coatings with addition of boron and silicon

Thermal stability and oxidation behavior of AlTiN, AlCrN and AlCrSiWN coatings

Effect of V-addition on the Thermal Stability and Oxidation Resistance of CrAlN Coatings

Influence of TiN and ZrN Insertion Layers on the Microstructure, Mechanical and Thermal Properties of Cr–Al–N Coatings

Tribological Properties of Nanostructured TiAlN/W2N Multilayer Coating Produced by PVD

Thermal and Thermo-Mechanical Properties of Ti–Al–N and Cr–Al–N Coatings

Microstructure, Mechanical Performance, Thermal Stability, and Oxidation Resistance of Alcrn/Alcrbn Nano-Multilayer Coating

Effect of CrMoN addition on the thermal stability and cyclic impact resistance of TiVN coatings

Influence of Ni-addition on Mechanical, Tribological Properties and Oxidation Resistance of AlCrSiN Coatings

Comparative study on mechanical and tribological properties of Cr–Al–N and Cr–Al–O coatings deposited by cathodic arc evaporation

Thermal Stability and Oxidation Resistance of V-alloyed TiAlN Coatings

Preface to the Special Issue of Selected Papers from ThinFilms2014

Improvement of the Mechanical, Tribological Properties and Oxidation Resistance of AlCrVN Coatings by Nb Alloying