Phase composition, structural and magnetic properties of core-shell nanoparticles based on iron carbide Fe 3 C synthesized by the sol-gel method
V.A. Zayakhanov,S.S. Starchikov,M.V. Lyubutina,Chun-Rong Lin,Ying-Zhen Chen,Bing-Yi Chen,A.L. Vasiliev,I.S. Lyubutin
DOI: https://doi.org/10.1016/j.jallcom.2023.172965
IF: 6.2
2023-12-09
Journal of Alloys and Compounds
Abstract:A new one-stage anhydrous sol-gel method for the synthesis of core-shell nanoparticles based on Fe 3 C and carbon is proposed. Powders of iron (III) nitrate Fe(NO 3 ) 3 ·9 H 2 O and polyacrylonitrile (PAN) were used as initial reagents, dimethylacetamide (DMAc) was used as a solvent. The synthesis was carried out in an inert argon atmosphere at various temperatures ( T syn ) up to 1000 °C. The morphology, structure, elemental and phase compositions, magnetic and electronic properties of the obtained core-shell nanocomposites were studied by various methods, such as X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM), energy dispersive X-ray spectroscopy (EDXS), Raman and Mössbauer spectroscopy, and magnetometry. It was found that at temperatures T syn ≈ 400–500 °C, iron oxide γ-Fe 2 O 3 predominates in the synthesis product. At T syn ≈ 600–700 °C, iron carbide Fe 3 C is formed, whose content increases and reaches a maximum value (about 75%) with increasing T syn to 800–1000 °C. At T syn ≈ 1000 °C, nanocomposites of the core@shell type – Fe 3 C@C and Fe 2 O 3 @C, as well as those with a double shell Fe 3 C@Fe 2 O 3 @C – are formed. In the Fe 3 C@Fe 2 O 3 @C composites, Fe 3 C is a core, Fe 2 O 3 and carbon C are shells. As T syn increases from 500 °C to 1000 °C, the amount of iron oxide γ-Fe 2 O 3 decreases, and at T syn ≈ 1000 °C, γ-Fe 2 O 3 oxide completely transforms into α-Fe 2 O 3 . In the sample synthesized at T syn ≈ 1000 °C, particles with a crystallite size of 29.6 nm exhibit magnetic properties with the highest saturation magnetization value of 68 emu/g. The temperature dependence of the magnetization M(T) of this sample has a specific character – there are three sharp drops at temperatures close to the N é el/Curie point for bulk Fe 3 C, Fe 3 O 4 , and α-Fe. Such peculiar behavior of magnetization seems to be important, since it can find application in technology
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering