Abstract:In order to realize the utilization of coal-fired solid waste and captured carbon dioxide, the effects of ratio of solid waste, mineralized curing pressure and mineralized curing temperature on the compressive strength and carbon fixation rate of aerated concrete were studied, with the coal-based waste, coal ash and desulfurization gypsum as the main raw materials and slag as the supplementary cementitious material. The crystal phase structure and micro morphology under different mineralized curing conditions were analyzed by XRD and SEM, and the effect of different mineralized curing conditions on the pore structure of aerated concrete was studied by MIP. The experimental results show that the appropriate residual water/slag ratio is helpful to improve the CO 2 fixation rate and early compressive strength of aerated concrete. When the CO 2 curing pressure increases from 0.05 MPa to 1.00 MPa, the carbon fixation rate increases by 24.8%, and the compressive strength increases first and then decreases. When the curing pressure is 0.1 MPa, the maximum compressive strength is reached. With the CO 2 curing temperature rising from 25 ℃ to 105 ℃, the carbon fixation rate and compressive strength increases first and then decreases. The carbon fixation rate reaches maximum of 7.21% at 45 ℃, and the compressive strength reaches maximum of 3.53 MPa at 65 ℃. According to analysis of XRD and SEM, the major mineralized products are CaCO 3 , which mainly exist in the form of calcite and vaterite. Higher curing pressure（≥0.2 MPa） is likely to cause micro-cracks at the product interface. With the increase of curing temperature, the mineralized products and hydrated products appear simultaneously. According to MIP analysis, the influence of mineralized curing on the pores of aerated concrete can be divided into two aspects: on the one hand, CaCO 3 and other products with small particle size can fill the pores of 10-50 nm, on the other hand, reaction heat of mineralization and volumetric expansion of products can cause the increase of 30-60 μm pores. The microstructure can be optimized by increasing the curing temperature, which can make the distribution of pores more uniform.

Carbonation reaction properties and reaction mechanisms of red mud under different carbon dioxide pressures

Carbonation Curing of Industrial Solid Waste‐based Aerated Concretes

Control of Carbon Dioxide Sequestration by Mechanical Activation of Red Mud

Particle Carbonation Kinetics Models and Activation Methods under Mild Environment: the Case of Calcium Silicate

Reaction characteristics of CO2 captured by red mud

Sustainable Building Material from CO2 Mineralization Slag: Aggregate for Concretes and Effect of CO2 Curing

Enhanced Carbonation Curing of Cement Pastes with Dolomite Additive

Study on the Dealkalization Technics of Bayer-process Red Mud with CO_2 by Carbonation

Effects of Red Mud on Workability and Mechanical Properties of Autoclaved Aerated Concrete (AAC)

Application of red mud in carbon capture, utilization and storage (CCUS) technology

Red Mud As a Carbon Sink: Variability, Affecting Factors and Environmental Significance.

Removal of Alkali in the Red Mud Using Co2 at Ambient Conditions

Strengthening Mechanism of Red Mud with Calcium Oxide

An Overview on the Influence of Various Parameters on the Fabrication and Engineering Properties of CO2-cured Cement-Based Composites

Experimental study on the macroscopic and microscopic properties of cement paste backfill after treatment with carbon dioxide carbonize filling slurries during the mixing process

Research on the Biogas Production Mechanism of Mudstone in the Qaidam Basin under Different CO2 Pressures

Experimental Study on the Dealkalization of Red Mud Waste from Bayer Process by CO2Gas Floatation

Capture of Carbon Dioxide with Red Mud

Study on formulation of aerated concrete by CO2 mineralization using coal ash

Synergistic CO2 mineralization using coal fly ash and red mud as a composite system

Synergistic Promotion for CO2 Absorption and Solvent Regeneration by Fine Waste Red Mud Particles on in Amine-Based Carbon Capture: Performance and Mechanism