Abstract:Silicon nanotubes (SNTs) are very attractive in the fields of energy, catalysis, and sensors, but a facile template- and/or catalyst-free preparation method is still absent. Herein, we study a controllable and cost-effective approach for preparing SNTs by electrochemically reducing layer-structured calcium silicate (CaSiO3) in molten CaCl2/NaCl without any template and catalyst. The underlying mechanism of the SNT formation is uncovered: the layer-structured CaSiO3 is first electrochemically exfoliated into SiOx (0 < x < 2) sheets while releasing CaO into the molten salts, and then the SiOx sheets are electrochemically reduced and simultaneously crimped into SNTs. The diameter (120–312 nm) and wall thickness (∼40 nm) of the SNTs can be tailorable by manipulating the reduction potential between −1.28 and −1.48 V (vs Ag/AgCl). Lastly, the electrolytic SNTs show a high lithium storage capacity of 3737 mAh g–1 at 0.2 A g–1, a high rate capability of 1371 mA h g–1 at 10 A g–1, and stable cycling with a capacity of 974 mAh g–1 after 600 cycles at 1 A g–1. Overall, the template- and catalyst-free electrochemical method provides a straightforward and facile way to prepare SNTs with a brand-new mechanism that can be applied to other tubular structure materials.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c07031?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c07031</a>.TEM image, SAED, and EDS of CaSiO3 electrolyzed at −1.1 V for 12 h; XRD patterns of the quartz substrate that holds the samples; SEM images and Raman spectrum of electrolytic products at −1.39 V for 12 h; SEM images of the electrolytic products at −1.35 V for 12 h; SEM image of the electrolysis product of silica particles; SEM images and EDS spectrum of samples prepared at −1.39 V for 3 and 6 h; CV curves of the SNT electrode; cycling performance of commercial SNPs; cycling performance of commercial SNPs; SEM images of SNT and SNP electrodes before and after cycling; charge/discharge profile and cycling performance of the SNTs||LCO full cell at 1 C (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c07031/suppl_file/am1c07031_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Self‐Assembly of Silicon Nanotubes Driven by a Biphasic Transition from the Natural Mineral Montmorillonite in Molten Salt Electrolysis

Electrochemical Conversion of Silica Nanoparticles to Silicon Nanotubes in Molten Salts: Implications for High-Performance Lithium-Ion Battery Anode

Fabricating Silicon Nanotubes by Electrochemical Exfoliation and Reduction of Layer-Structured CaSiO3 in Molten Salt.

Fabricating Silicon Nanotubes by Electrochemical Exfoliation and Reduction of Layer-Structured CaSiO 3 in Molten Salt

Porous Si@C Coaxial Nanotubes: Layer-by-layer Assembly on ZnO Nanorod Templates and Application to Lithium-Ion Batteries

Rapid Fabrication of Porous Silicon/carbon Microtube Composites As Anode Materials for Lithium-Ion Batteries

Silicate-Mediated Electrolytic Silicon Nanotube from Silica in Molten Salts

Synthesis of carbon nanotubes-supported porous silicon microparticles in low-temperature molten salt for high-performance Li-ion battery anodes

Silicon nanotube anode for lithium-ion batteries

A Hollow Silicon Nanosphere/Carbon Nanotube Composite as an Anode Material for Lithium-Ion Batteries

Lithium-storage properties of SiO 2 nanotubes@C using carbon nanotubes as templates

A ′′Reinforced Concrete′′ Structure of Silicon Embedded into an In Situ Grown Carbon Nanotube Scaffold as a High-Performance Anode for Sulfide-Based All-Solid-State Batteries

Meso-porous silicon-coated carbon nanotube as an anode for lithium-ion battery

Facile Molten Salt Synthesis of Carbon-anchored TiN Nanoparticles for Durable High-rate Lithium-ion Battery Anodes

Chelation-Assisted formation of carbon nanotubes interconnected Yolk-Shell Silicon/Carbon anodes for High-Performance Lithium-ion batteries

Silicon micron cages derived from a halloysite nanotube precursor and aluminum sacrificial template in molten AlCl<sub>3</sub> as an anode for lithium-ion batteries

Synthesis of 3D stacked silicon nanosheets via electrochemical reduction of attapulgite in molten salt for high-performance lithium-ion batteries anode

A Facile, One-Step Synthesis of Silicon/Silicon Carbide/Carbon Nanotube Nanocomposite as a Cycling-Stable Anode for Lithium Ion Batteries

In situ Preparation of SiOx/Carbon Nanotube Composite Films with Excellent Mechanical and Electrochemical Properties as an Anode Material for Lithium‐Ion Batteries

Controllable Preparation to Boost High Performance of Nanotubular SiO2@C as Anode Materials for Lithium-Ion Batteries

Three-Dimensional Porous Si and SiO2 with In Situ Decorated Carbon Nanotubes As Anode Materials for Li-ion Batteries