The Crystal Structure of Iron-Nickel Alloys

L. W. McKeehan

DOI: https://doi.org/10.1103/physrev.21.402

1923-04-01

Physical Review

Abstract:Crystal structure and density of a complete series of pure iron-nickel alloys. —Fourteen alloys were prepared by melting together Armco iron and electrolytic nickel, then swaging the castings and drawing and rolling into thin tapes. X-ray diffraction patterns were obtained with these, after various heat treatments. With from zero to 25 per cent Ni, the structure is chiefly body-centered-cubic, the parameter a increasing from 2.872 × 10-8 cm for pure iron to about 2.89 × 10-8 cm. With from zero to 70 per cent Fe, the structure is chiefly face-centered-cubic, the parameter a increasing from 3.510 for pure nickel to about 3.60 × 10-8 cm. Around 30 per cent Ni, either structure is on the verge of instability and both or either may exist. Cold work tends slightly to increase the parameter. The densities of pure iron and nickel crystals come out 7.775 and 8.953 gm/cm3, respectively. Speculations regarding atoms of iron and nickel.—It is probable that nickel atoms differ from iron atoms in possessing six electron orbits of a certain type in place of four. The behavior of these atoms in forming crystals is consistent with the idea that the directions of closest approach in either pure metal are the normals to the planes of these orbits and that in the intermediate directions, twelve for iron and eight for nickel, the atoms cannot approach so closely, these directions determining the positions of what we may call protuberances on the atoms. The electrons which are responsible for cohesion may be not the valence electrons but those in a deeper layer.