Abstract:The interface bonding strength between adjacent melt lines formed in the melt-extrusion-based 3D printing (ME3DP) process largely governs the mechanical properties of the as-printed parts. But this normally leads to mechanical anisotropy of which the mechanism is not very clear. In this work, based on the investigation of the temperature attenuation behavior of newly deposited thermoplastic polyurethane (TPU) melt in a ME3DP process, the mechanical dependence on the interface development was explored. First, the temperature attenuation of a newly deposited melt in an open environment was found to be well fitted by the Power-law function. Then the effect of envelope temperature on the tensile property of the as-printed TPU was studied using an electric-heating bed (EHB) which endowed the whole printed sheets with a temperature near EHB temperature. To explore the mechanism of mechanical anisotropy, tensile testing was then performed for the printed sheets in both longitudinal and transverse directions, respectively. Results showed that the ultimate tensile strength (UTS), as well as the elongation at break measured along the transverse direction, increased with the increase of EHB temperature, which was mainly attributed to the improved interface bonding. In comparison, the UTS along the longitudinal direction kept relatively stable, slightly increasing initially and then followed by a minor decrease. Of note is the fact that the mechanical properties of printed parts were governed simultaneously by both the wall-shear-induced orientation effect of molecular chains at the surface of the deposited melt line and the crystallization morphology inside the deposited molten filament was concluded in this work. A high envelope temperature not only promoted the molecular diffusion around the interface layer, enhanced the interface bonding, and overcome the mechanical anisotropy but also promoted the crystallization kinetics. The printed TPU with developed crystallized morphology exhibited improved yield stress in the longitudinal direction above a critical temperature. This work demonstrates an insight into the mechanical anisotropy of 3D-printed polymers, paving the way to print high-strength parts via ME3DP.

Microstructure and tensile properties of injection molded thermoplastic polyurethane with different melt temperatures

Viscoelastic Property Evolution of Thermoplastic Polyurethane During Annealing Treatment and Its Correlation with Segmental Crystallization

Investigation of tensile behavior and molecular structure of the thermoplastic polyurethane sheets injection molded at different mold temperatures

The Structure and Dynamic Properties of Thermoplastic Polyurethane Elastomer/Hindered Phenol Hybrids

Oriented distribution structure, interaction, and performance of thermoplastic polyurethane/selective hindered amine hybrids

Optimizing TPU performance: The role of mold temperature on injection molding of TPU

Effects of Physical Aging on Thermomechanical Behaviors of Poly(ethylene Terephthalate)-Glycol (PETG)

Optimizing Physical Aging in Poly(ethylene Terephthalate)-Glycol (PETG)

Thermomechanical Coupling in Glassy Polymers: an Effective Temperature Theory

Temperature-induced Evolution of Micro-structure and Chain Dynamics in Thermoplastic Polyurethane with Low Hard Segment Content as Studied by In Situ Synchrotron SAXS and Time-Domain NMR Experiments

An insight into the tensile anisotropy of 3D-printed thermoplastic polyurethane

Heating‐Responsive Shape‐Memory Effect in Thermoplastic Polyurethanes with Low Melt‐Flow Index

Evolution of ordered structure of TPU in high-elastic state and their influences on the autoclave foaming of TPU and inter-bead bonding of expanded TPU beads

Dependence of microstructure and properties of polypropylene/bromo‐isobutylene‐isoprene rubber thermoplastic vulcanizates on the molding process

Mechanical Properties of Additively Manufactured Thermoplastic Polyurethane (TPU) Material Affected by Various Processing Parameters

The Crystallisation, Microphase Separation and Mechanical Properties of the Mixture of Ether-Based TPU with Different Ester-Based TPUs

Effects of shear during injection molding on the anisotropic microstructure and properties of EPDM/PP TPV containing rubber nanoparticle agglomerates

Controlling Energy Dissipation During Deformation by Selection of the Hard-Segment Component for Thermoplastic Polyurethanes

Approach to Fabricating Thermoplastic Polyurethane Blends and Foams with Tunable Properties by Twin‐Screw Extrusion and Microcellular Injection Molding

Effect of Two Crystalline Forms on the Multiple Melting and Crystallization Kinetics of Thermoplastic Polyurethane

Effect of processing parameters, antistiction coatings, and polymer type when injection molding microfeatures