A Highly Efficient Silicone-Modified Polyamide Acid Binder for Silicon-Based Anode in Lithium-Ion Batteries

Qiang Zhang,Fengying Zhang,Meng Zhang,Yuxiu Yu,Shuxia Yuan,Yaodong Liu

DOI: https://doi.org/10.1021/acsaem.1c01294

IF: 6.4

2021-07-01

ACS Applied Energy Materials

Abstract:Silicon (Si) exhibits an excellent specific capacity and emerging application potential as anode material of lithium-ion batteries. However, Si anodes usually generate the huge volume expansion and the instability of the solid electrolyte interface, leading to performance degradation. Herein, a silicone-modified partially imidized polyamide acid (S-PA) is successfully synthesized, which shows excellent performances as the binder of a silicon-based electrode in lithium-ion batteries. The S-PA anodes exhibit high initial Coulombic efficiencies of above 87% and maintain over 98% in the following cyclic tests. At a current of 0.5 C, the initial discharge capacity of the S-PA-based electrode is as high as 2736 mAh g^–1 and remains at about 2295 mAh g^–1 over 200 cycles. The abundant chemical bonds in the S-PA binder contribute to the improvement of the interactions with silicon nanoparticles, maintain the electrode structural integrity, and facilitate the Li-ion diffusion during cycling. The results show that S-PA is a promising type of binder for silicon-based anodes as compared with commonly adopted PAA and PVDF.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c01294?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c01294</a>.TGA spectrum of synthesized binder, stress–strain curves, SEM images, electrical parameters obtained from fitting the impedance plots (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c01294/suppl_file/ae1c01294_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical,energy & fuels

What problem does this paper attempt to address?

This paper attempts to solve the key problems of silicon - based anode materials in the application of lithium - ion batteries, namely the huge volume expansion (up to 300%) caused by lithiation and delithiation of silicon - based anode materials during the charging and discharging process and the instability of the solid - electrolyte interface (SEI) layer. These problems will lead to the destruction of the electrode structure and the decline of performance, thus affecting the cycle life and overall performance of the battery.

To solve the above problems, the author synthesized a silane - modified partially imidized polyamic acid (S - PA) as a binder for silicon - based anode materials. By introducing flexible siloxane segments into the polyamide main chain, the S - PA binder can provide good adhesion and volume - expansion resistance. The experimental results show that the silicon - based anode materials using S - PA as a binder exhibit excellent cycle stability and high - capacity retention rate. Specifically:

- **High initial Coulombic efficiency**: The initial Coulombic efficiency of the S - PA - based electrode exceeds 87% and remains above 98% in subsequent cycle tests.
- **High capacity and long cycle life**: At a current density of 0.5 C, the initial discharge capacity of the S - PA - based electrode is as high as 2736 mAh g\(^{-1}\), and it can still maintain a capacity of about 2295 mAh g\(^{-1}\) after 200 cycles.
- **Good rate performance**: The S - PA - 15 electrode exhibits excellent rate performance at different current densities, and can maintain a relatively high specific capacity even at a high current density of 2 C.

In addition, the abundant chemical bonds in the S - PA binder help to improve the interaction with silicon nanoparticles, maintain the integrity of the electrode structure, and promote the diffusion of lithium ions during the cycle. These characteristics make S - PA a very promising binder for silicon - based anode materials, which has significant advantages compared with the commonly used PAA and PVDF.