Effect of graphene addition on a borosilicate glass/alumina composite for LTCC technology

Yuanyuan Lv,Lan Zhang,Shuquan Yang,Zhihua Wang,Lin Chen,Jun Sun,Xiaoxiao Li,Jianjun Ding,Kang Zheng,Yi Gong,Xian Zhang,Xingyou Tian

DOI: https://doi.org/10.1016/j.ceramint.2021.01.167

IF: 5.532

2021-05-01

Ceramics International

Abstract:<p>The effect of graphene nanoplatelets (GNPs) on the thermal conductivity of low temperature co-fired ceramic (LTCC) materials based on ZnO–B₂O₃–Na₂CO₃–Al₂O₃–SiO₂ (ZBNAS) glass/Al₂O₃ composites sintered at 850 °C for 2 h were systematically investigated. The sintered sheets were prepared by standard tape casting process and solid phase sintering. The microstructure and phase composition of the sintered sheets were characterized by SEM and XRD, respectively. With the addition of 0.75 wt% GNPs, the thermal conductivity of the sintered sheet was increased from 3.91 to 7.85 W/(m·K). Meanwhile, the 0.75 wt% GNPs-Al₂O₃-ZBNAS glass (GNPs(0.75)/Al₂O₃/ZBNAS) composite achieved low dielectric constant of 5.16 and dielectric loss of 0.13 at 18 GHz. The coefficients of thermal expansion (CTE) of the sintered sheets decrease first and then increase. The CTE of GNPs(0.75)/Al₂O₃/ZBNAS composite is −7.13 × 10⁻⁶ °C⁻¹ and 3.20 × 10⁻⁶ °C⁻¹ at low temperature (25–80 °C) and high temperature (80–200 °C), respectively. The obtained graphene-based LTCC materials are promising candidates in terms of the potential application of electronic devices with high thermal conductivity requirement.</p>

materials science, ceramics