Effects of carbon short-range structure and Co-based catalyst on solid-phase synthesis of calcium carbide at moderate temperatures
Zhenpan Chen,Pengpeng Cai,Jie Cai,Shuoqi Hao,Yujie Chen,Wenguang Yu,Feifei Xu,Kuiyi You,He’an Luo
DOI: https://doi.org/10.1016/j.jssc.2022.123012
IF: 3.3
2022-05-01
Journal of Solid State Chemistry
Abstract:Owing to the thermodynamic and kinetics restrictions, traditional electric arc method for calcium carbide (CaC2) synthesis is operated at very high temperature (∼2200 °C), which is an energy intensive (∼4000 kW·h/(t CaC2)) process and brings strict requirements to reactor design. Herein, to improve the calcium oxide (CaO) conversion rate, the short-range structure tailored active carbon (AC) material and CoOx as a catalyst were used for solid-phase synthesis of CaC2. It was found that the conversion of CaO could be increased by about 4-fold when using tailored AC with decreased impurity of H, S, N heteroatoms, increased content of disordered carbon atoms, expanded (002) crystal facet and C–C bond length. Compared with blank test, 5 wt% Co3O4 as a cobalt catalyst precursor that added into CaO-AC mixture can further increase the CaO conversion by ∼20% under optimal conditions and the onset temperature of solid-phase reaction decreases to ∼1620 °C. This catalytic function is assumed to be related with the enhanced chemical reaction at the solid-solid interface of CaO and AC reactants, increased mixed ionic and electric conductivity (MIEC) of bulk. Our work demonstrates that the short-range structure of carbon material is an essential factor to determine its reactivity and the catalytic function is still necessary and important in solid-phase synthesis of CaC2 even at high temperatures.
chemistry, physical, inorganic & nuclear