Abstract:This work aimed at evaluating the effect of nickle (Ni) dopant on the catalytic performance of Co3 O4 catalyst for abatement of harmful carbon monoxide (CO), a resistance toward sintering and durability of catalytic activity were also pursued. Choose the Co(NO3 )2 ×6H2 O(aq) as precursor and NaOH as precipitant to prepare cobalt oxide (Co3 O4 ) with precipitation method, then calcined at 300 and 500 °C, separately (named as C3 and C5). The Ni dopant (0.1 ~ 5 wt%) was added by deposited precipitation through Ni(NO3)2 ×6H2 O(aq) with drop wisely added NaOH(aq) into suspended Co3 O4 solution, then put the NaOCl for oxidation to obtain series 0.1%Ni-Co3 O4 , 0.2%Ni-Co3 O4 , 1%Ni-Co3 O4 and 5%Ni-Co3 O4 catalysts. All catalysts were characterized through BET, XRD, TEM/SEM, Raman, ICP and TPR instruments, and evaluated the catalytic performance of CO oxidation with a self-devised fluidized micro-reactor. It was observed that the calcination temperature and loading of dopant remarkably influenced the physicochemical characteristics and catalytic performance of the catalysts. Preferential catalyst was obtained for calcination at 300 °C and loading of Ni dopant below 1%. The doping of Ni on the surface of Co3 O4 enhanced the performance due to the inducing of synergistic effect between Co3 O4 and NiO, while the excessive NiO incorporated to the surface constrained the activity due to the abundant NiO on the surface, overlaying the active sites caused the decreasing of surface area and reducible capacity. Among these series Ni-Co3 O4 catalysts, the 0.2%Ni-Co3 O4 (C3) catalyst behaved an eminent activity with T50 of 98 °C and durability without apparent deactivation for 50 hr reaction at 125 °C. The excellent performance is primarily attributed to the synergistic effect and formation of NiCo2 O4 composite oxide.

Research over the effect of activated carbon treated with calcium nitrate solution on the catalytic ability in the reduction of Co(III)Triethylenetetramine

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

DFT Study of the Effect of Ca on NO Heterogeneous Reduction by Char

Nitrogen Doping of Activated Carbon Loading Fe2O3 and Activity in Carbon-Nitric Oxide Reaction

Reduction of [fe(iii)edta]− Catalyzed by Activated Carbon Modified with Ammonia Solution

Reduction of NO by La_2O_3-loaded activated carbon

Regeneration of Hexamminecobalt(Ii) under the Catalysis of Activated Carbon Treated with K2s2o8 Solution

Effect of Nitrogen Doping on the Reduction of Nitric Oxide with Activated Carbon in the Presence of Oxygen

Adsorption–Reduction Behavior of Co(NH3) on Activated Carbon

Reduction of [fe(iii)edta]− Catalyzed by Activated Carbon Modified with KOH Solution

Regeneration of Hexamminecobalt(ii) under the Catalysis of Activated Carbon Modified with ZnCl2 Solution

Effect of Pretreatment Method of Activated Carbon on the Catalytic Reduction of NO by Carbon over CuO

Removal of NO with Fe(II)NTA solution catalyzed by the carbon treated with ethylenediamine

Direct Promotion Effect of Fe on No Reduction by Activated Carbon Loaded with Fe Species

Kinetics of the [Fe(iii)-Edta]− Reduction by Sulfite under the Catalysis of Activated Carbon

Effect of K-Modified Blue Coke-Based Activated Carbon on Low Temperature Catalytic Performance of Supported Mn–Ce/Activated Carbon

Regeneration of Hexamminecobalt(ii) Catalyzed by Activated Carbon Treated with KOH Solutions

Reduction of Hexamminecobalt (iii) Catalyzed by Coconut Activated Carbon

ABATEMENT OF HARMFUL CARBON MONOXIDE OVER THE NICKLE DOPED CO3 O4 CATALYST

Carbon deposition enhanced selective catalytic reduction of nitric oxide by a new catalytic process as well as increasing reducibility of catalyst

The effect of carbonized zeolitic imidazolate framework-67 (ZIF-67) support on the reactivity and selectivity of bimetal-catalytic aqueous NO 3 − reduction