Effect of the Austenitizing Temperature on Microstructure Evolution and Impact Toughness of a Novel Bainite Ductile Iron

Yongjin Wang,Yingchao Zhang,Renbo Song,Liang Huang,Yu Pei
DOI: https://doi.org/10.1007/s12540-020-00893-5
IF: 3.451
2020-11-05
Metals and Materials International
Abstract:<span class="a-plus-plus abstract-section id-a-sec1"><p class="a-plus-plus">The effect of austenitizing temperature on microstructure evolution and impact toughness of a newly developed Fe–3.0C–2.8Si–2.0Mn–0.9V–0.2Cr bainite ductile iron was investigated in this research. The ductile iron specimens were heat treated under different continuous cooling process, involving austenitizing between 900 and 980 °C and followed tempering at 200 °C. Optical microscopy, X-ray diffraction, scanning electron microscope and transmission electron microscope tests were conducted to investigate the microstructure evolution. Impact toughness and Rockwell hardness were measured. The results showed that the microstructure of the ductile iron mainly consisted of graphite, acicular bainite and retained austenite after continuous cooling process. The austenitizing temperature could change the volume fraction and size of bainite and retained austenite. There existed a C-area, where retained austenite accumulated near the graphite, except for specimen austenitized at 920 °C. The impact toughness of specimens increased first and then get worse with the increasing of austenitizing temperature. The impact toughness was related with the volume fraction of bainite and the morphology of retained austenite. The fracture mechanism of the bainite ductile iron belonged to cleavage fracture. Chunky graphite acted as the source of microcrack during the impact process. The bulky retained austenite behaved as a prior path for the microcrack propagation, while the bainite and thin filmy retained austenite limited its propagation.</p></span><span class="a-plus-plus abstract-section id-a-sec2 outputmedium-online"><h3 class="a-plus-plus">Graphic </h3></span>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper primarily investigates the microstructural evolution of novel bainitic ductile iron under different austenitizing temperatures and its impact on impact toughness. Specifically, the paper explores the following issues: 1. **Material Design and Preparation**: A novel Fe-3.0C-2.8Si-2.0Mn-0.9V-0.2Cr bainitic ductile iron was designed and subjected to heat treatment through different continuous cooling processes, including austenitizing treatment in the range of 900 to 980°C, followed by tempering at 200°C. 2. **Microstructural Analysis**: The microstructural analysis of samples under different heat treatment conditions was conducted using optical microscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). 3. **Performance Testing**: The Rockwell hardness and impact toughness of the samples were measured. 4. **Relationship Between Microstructure and Performance**: It was found that the microstructure of this novel ductile iron mainly consists of graphite, acicular bainite, and retained austenite. The austenitizing temperature affects the volume fraction and size of bainite and retained austenite. Additionally, there is a special region (C region) where retained austenite accumulates near the graphite, except for the samples austenitized at 920°C. 5. **Impact Toughness Variation**: As the austenitizing temperature increases, the impact toughness of the samples first increases and then decreases. The impact toughness is related to the volume fraction of bainite and the morphology of retained austenite. 6. **Fracture Mechanism**: The fracture mechanism of bainitic ductile iron is cleavage fracture. Chunky graphite acts as the origin of microcracks during impact. Chunky retained austenite serves as the preferential path for microcrack propagation, while bainite and film-like retained austenite restrict crack propagation. In summary, this paper systematically studies the effect of different austenitizing temperatures on the microstructure and impact toughness of novel bainitic ductile iron, revealing how these factors collectively influence the final performance of the material.