Revealing the Enhancement of Li Plating/Stripping Efficiency in the TEGDME-based Low-concentration Electrolytes for Anode-free Lithium Metal Batteries

Yushen Wang,Hidenori Noguchi
DOI: https://doi.org/10.1039/d4cp02755h
IF: 3.3
2024-09-25
Physical Chemistry Chemical Physics
Abstract:Anode-free lithium metal batteries (AFLMBs) have attracted great attention owing to their higher energy density than conventional lithium metal batteries (LMBs). Unfortunately, the present AFLMBs still suffer from overall inferior Coulombic efficiencies (CEs) to those of LMBs due to the more severe dendrite growth and more unstable solid-electrolyte interface (SEI) formation at the anode side, which is an urgent issue to be solved. In this study, we explored the effect of increasing concentration and adding 0.1M LiNO3 additive on SEI layer and on Li plating/stripping efficiency using the low-concentration (0.4 M) tetraethylene glycol dimethyl ether (TEGDME)-based electrolyte in an AFLMB anode half-cell configuration. The influence of the oxidative subsequent SEI formation above 2.2 V vs. Li/Li+, called as "OSS", was also discussed. It was found that Li plating/stripping stability was greatly improved by either blocking OSS or adding LiNO3, while increasing concentration to 2.0 M did not function well. The formation of the protective Li2O-based subsequent SEI layers when blocking reaction OSS is considered to guarantee the improved stability of Li plating/stripping, while LiNO3 additive helps sustaining the existence of Li2O even with the occurrence of OSS, therefore substantially improving the CE performance. Meanwhile, the effect of increasing concentration to 2.0 M in the existence of 0.1 M LiNO3 additive shifted the dominant SEI species from Li2O to LiF, further assuring the enhanced CE performance in the low-concentration TEGDME-based electrolytes.
chemistry, physical,physics, atomic, molecular & chemical
What problem does this paper attempt to address?