Convenient hydrothermal treatment combining with "Ship in Bottle" to construct Yolk-Shell N-Carbon@Ag-void@mSiO 2 for high effective Nano-Catalysts
Nana Zhao,Jianlong Wang,Shaofeng Song,Chao Li,Juan Wang,Xin Li,Zhicheng Pan,Jinfeng Yuan,Lei Zhu,Mingwang Pan
DOI: https://doi.org/10.1016/j.apsusc.2023.157158
IF: 6.7
2023-04-05
Applied Surface Science
Abstract:More active sites will be exposed when noble metal particles are loaded on the core of yolk-shell nanospheres (NM-YSNS) to give higher metal utilization rate, catalytic activity, and good recycle stability. Herein, we adopt an efficient strategy to access the high-performance NM-YSNS via "ship in bottle" mindset on loading Ag nanoparticle on the core surface of core–shell structure accurately and the core shrinkage on forming yolk-shell structure. First, we systematically investigated the mechanism of SiO 2 coating 3-aminophenol- co -formaldehyde nanoparticles to generate 3-aminophenol- co SiO 2 core–shell nanospheres ( 2 CSNS). Interestingly, the core surface of 2 CSNS became uneven after hydrothermal process, which provided positions for Ag, then additional Ag + could reach the 3-APF surface through the mSiO 2 shell and be in situ reduced into Ag particles by –NH- and –NH 2 there. Similarly, the @mSiO 2 CSNS were prepared successfully. After carbonizing @mSiO 2 CSNS, the @mSiO 2 YSNS was obtained. The NM-YSNS catalyst had a high specific surface area of 258.8 m 2 g −1 , mSiO 2 shell of 3.8 nm mesoporous size, and core loaded with Ag particles firmly, showing a high turnover frequency of 137.08 h −1 and good recycle stability in catalytic reduction of 4-nitrophenol for preparing 4-aminophenol.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films