Abstract:We report the dendrimer-mediated synthesis and shape evolution of gold–silver alloy nanoparticles (Au–Ag alloy NPs) with different metal compositions. In this study, amine-terminated generation 5 poly(amidoamine) dendrimers were used as stabilizers to prepare Au–Ag alloy NPs with different gold atom/silver atom/dendrimer molar ratios without the assistance of additional reducing agents. Following a one-step acetylation reaction to transform the dendrimer terminal amines to acetyl groups, a series of Au–Ag alloy NPs with surface acetyl groups were formed. The alloy NPs before and after acetylation reaction were characterized using 1H NMR, UV–vis spectrometry, transmission electron microscopy, inductively coupled plasma-optical emission spectroscopy, and X-ray absorption coefficient measurements. We showed that the optical property, the size, and the morphology of the bimetallic NPs were greatly affected by the metal composition and their surface modification. At the constant total metal atom/dendrimer molar ratio, the alloy NPs experienced a shape evolution from spherical particles and polyhedrons to curved nanowires with the Au content. Acetylation of the dendrimer terminal amines seemed to thicken the nanowires. The formed Au–Ag alloy NPs were stable at different pH (pH 5–8) and temperature (4–50°C) conditions. X-ray absorption coefficient measurements showed that the attenuation intensity of the alloy NPs was dependent on both the metal composition and surface functional groups. At a given metal composition, the X-ray attenuation intensity of the binary NPs was enhanced after acetylation. The formed metal alloy NPs with tunable size and shape prepared using the dendrimer stabilizers may be used in a range of applications in catalysis, sensing, and biomedical sciences.

Synthesis of thermally stable and highly active bimetallic Au-Ag nanoparticles on inert supports

Bimetallic Ag-Au Nanowires: Synthesis, Growth Mechanism, and Catalytic Properties.

Synthesis of Highly Dispersed and Highly Stable Supported Au–Pt Bimetallic Catalysts by a Two-Step Method

Nanoengineering of Aggregation-Free and Thermally-Stable Gold Nanoparticles in Mesoporous Frameworks

AuAg bimetallic nanoparticles film fabricated based on H2O2-mediated silver reduction and its application.

Directed Synthesis of Well Dispersed and Highly Active AuCu and AuNi Nanoparticle Catalysts

Adding Two Active Silver Atoms on Au25 Nanoparticle

Synthesis by Replacement Reaction and Application of TiO2‐Supported Au–Ni Bimetallic Catalyst

Low-Temperature Solution-Phase Synthesis of NiAu Alloy Nanoparticles Via Butyllithium Reduction: Influences of Synthesis Details and Application As the Precursor to Active Au-NiO/SiO2 Catalysts Through Proper Pretreatment

Facile Synthesis of Supported AuNi and PtNi Bimetallic Nanomaterials and Their Enhanced Catalytic Properties

The region-specific segregation and catalytic activity of gold-silver nanoparticles.

Toward Monodispersed Silver Nanoparticles with Unusual Thermal Stability.

Reduced Sintering of Mass-Selected Au Clusters on SiO2by Alloying with Ti: an Aberration-Corrected STEM and Computational Study

Synthesis of Cu@Ag Core–shell Nanoparticles for Characterization of Thermal Stability and Electric Resistivity

Biosynthesis of Bimetallic Au–Ag Nanoparticles Using Escherichia coli and its Biomedical Applications

Synthesis of Ag@Au nanoparticles and their characterization of high temperature in-situ XAFS

A Facile and Controllable Strategy to Synthesize Au-Ag Alloy Nanoparticles Within Polyelectrolyte Multi Layer Nanoreactors Upon Thermal Reduction

A novel strategy to synthesize bimetallic Pt–Ag particles with tunable nanostructures and their superior electrocatalytic activities toward the oxygen reduction reaction

Dendrimer-mediated Synthesis and Shape Evolution of Gold–silver Alloy Nanoparticles

Surface-Plasmon-Mediated Alloying for Monodisperse Au-Ag Alloy Nanoparticles in Liquid

Fabrication of SBA-15 supported Ag@Au-Ag metal-core/alloy-shell nanoparticles for CO oxidation