Synthesis of Ag@Au nanoparticles and their characterization of high temperature in-situ XAFS

Haiyang WANG,Tao YAO,Shoujie LIU,Xiangcun CHEN,Chaoyang KANG,Zhihu SUN,Shiqiang WEI,Guoqiang PAN

2012-01-01

Abstract:Ag@Au core-shell nanoparticles were synthesized via chemical liquid phase reduction method. They were characterized by UV-Vis absorption spectroscopy, transmission electron microscopy (TEM), differential scanning calorimetry (DSC) and X-ray absorption fine structure (XAFS) spectroscopy. The Ag@Au nanoparticles are of uniform and stable monodisperse, with an average size of the Ag core of about 8 nm, and the Au shell thickness of about 3.5 nm. DSC spectra show that core-shell particles are the most dramatic diffusion in the alloying process around 300°C, and the alloy is completely formed at 500°C. From the high temperature in-situ XAFS and the RSF curves, significant changes are clearly seen in the local structure of Au atoms in the alloying process. By fitting the data with replacement method, the Au-Au bond length gradually becomes longer from 2.86 Å to 2.89 Å and the coordination bond from 8.0 to 6.1, with 2.1 Au-Ag coordination bonds and increased degree of disorder, at the alloy formation. The alloy process is mainly based on subrogation diffusion.