Abstract:A facile approach is developed to synthesize carbon‐supported, high‐loading, well‐distributed, and ultra‐small nanoparticles (NPs) via tuning the surface electrostatic effect to induce strong interaction between carbon support and metal salt precursors. This approach can be extended to various alloy compositions and different supports, thereby offering a general strategy for developing high‐quality supported NPs for various applications. Carbon‐supported nanoparticles (NPs) are widely used as catalysts in fuel cells and electrolyzers. While it is well known that NPs with smaller size and higher loading often lead to better catalytic activity, they remain challenging to synthesize due to the weak control over the surface properties of the support. Herein, a facile approach to synthesize carbon‐supported, high‐loading, and ultra‐small Pt3Ni NPs via applying thermal shock on strongly interacted carbon support with metal salt is reported. Specifically, sodium citrate is introduced into the precursor solution and substrate mixture, which induces strong electrostatic effect between metal salts and carbon particles that markedly improves precursor anchoring and dispersion, thereby achieving high particle loading as well as small size and distribution. As a proof‐of‐concept, the synthesis of Pt3Ni NPs supported on carbon black with particle size of 1.56 ± 0.36 nm at 30 wt% loading and 1.66 ± 0.56 nm at 40 wt% loading is reported, where the sizes are among the smallest while the loadings are among the highest in the literature. This approach can be readily extended to many compositions and substrates, with tunable particle size and loading, thereby substantially expanding the synthesis space for NP catalysts in various electrochemical applications.

High-Temperature Synthesis of Carbon-Supported Bimetallic Nanocluster Catalysts by Enlarging the Interparticle Distance

Ultrafine Nanoparticle-Supported Ru Nanoclusters with Ultrahigh Catalytic Activity.

Enhancing the Catalytic and Electrocatalytic Properties of Pt-based Catalysts by Forming Bimetallic Nanocrystals with Pd

Synthesis of Carbon-Supported Sub-2 Nanometer Bimetallic Catalysts by Strong Metal–sulfur Interaction

A Sulfur-Fixing Strategy Toward Carbon-Supported Ru-Based Bimetallic Nanocluster Catalysts

Synthesis of Rhodium Intermetallic Catalysts by Enlarging the Inter-Particle Distance on High-Surface-area Carbon Black Supports.

Facile Synthesis of Highly Dispersed and Well‐Alloyed Bimetallic Nanoparticles on Oxide Support

Aerosol Spray Drying Guided Synthesis of Ultrasmall Alloyed Bimetallic Nanoparticles Supported on Silica for Catalytic Semihydrogenation

Low-Temperature Solution-Phase Synthesis of NiAu Alloy Nanoparticles Via Butyllithium Reduction: Influences of Synthesis Details and Application As the Precursor to Active Au-NiO/SiO2 Catalysts Through Proper Pretreatment

A library of carbon-supported ultrasmall bimetallic nanoparticles

A Sulfur-Tethering Synthesis Strategy Toward High-Loading Atomically Dispersed Noble Metal Catalysts

Microporous Sulfur-Doped Carbon Atoms as Supports for Sintering-Resistant Platinum Nanocluster Catalysts

Nitrogen-fixing of ultrasmall Pd-based bimetallic nanoclusters on carbon supports

Sulfur stabilizing metal nanoclusters on carbon at high temperatures

Sintering behavior of carbon-supported Pt nanoparticles and the effect of surface overcoating

Solid-State Surface-Anchoring Strategy to Prepare Anti-Sintering Supported Metal Cluster Catalysts

Highly monodisperse Cu- and Ag-based bimetallic nanocrystals for the efficient utilization of noble metals in catalysis.

Bulky nanodiamond-confined synthesis of sub-5 nanometer ordered intermetallic Pd3Pb catalysts

Synthesizing Carbon‐Supported, High‐Loading, Ultra‐Small Pt3Ni Nanoparticles via Tuning the Surface Electrostatic Effect

Preparation, characterization and catalyses of light-transition-metal/noble-metal bimetallic alloy nanoclusters

Colloidal noble-metal and bimetallic alloy nanocrystals: a general synthetic method and their catalytic hydrogenation properties.