Abstract:Ni-MgO dual function materials (DFMs) show promise for integrated CO2 sorption and methanation. To improve CO2 sorption capacity, Ni-MgO DFMs are promoted with alkali metal nitrates. However, the high catalyst reduction temperature will result in high energy consumption, huge temperature gap between reduction (similar to 650 degrees C) and CO2 sorption and methanation (similar to 300 degrees C), and the loss of alkali metal nitrates. In this work, we prepared a Ni/CeO2 catalyst and investigated the effect of reduction temperature on its structure-property relationships in CO2 methanation, aiming to lower the reduction temperature to an isothermal level that matches CO2 methanation. Results indicated that the reduction temperature fell from over 650 to 300 degrees C, and Ni/CeO2 reduced at 300 degrees C featured high CO2 conversion (72.7%) and CH4 selectivity (98.9%). The CO2 methanation activity of Ni/CeO2 declined significantly when the reduction temperature exceeded 400 degrees C. The formation of more oxygen vacancy defects due to the interaction between NiO and CeO2 promoted the reduction of NiO species at lower temperatures. The declined CO2 methanation activity at high reduction temperatures was ascribed to the consumption of oxygen vacancies in catalyst reduction, and less defects were available for CO2 activation and methanation. An alkali metal nitrate promoted MgO adsorbent was physically mixed with Ni/CeO2 to construct (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs for integrated CO2 sorption and methanation. The DFMs could be facilely reduced at 300 degrees C, and this has made it possible to realize the isothermal operation of catalyst reduction and CO2 sorption and methanation in integrated CO2 capture and utilization (ICCU). The (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs reduced at 300 degrees C exhibited an impressive CO2 uptake of 2.74 mmol CO2/g DFMs and a great CH4 yield of 1.10 mmol CH4/g DFMs, and they could be a promising alternative to Ru-based DFMs with respect to their comparable CO2 sorption capacity and methanation activity and minimized cost of raw materials.

Recent progress of MgO-based materials in CO 2 adsorption and conversion: Modification methods, reaction condition, and CO 2 hydrogenation

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Insights into Nickel-Based Dual Function Materials for CO2 Sorption and Methanation: Effect of Reduction Temperature

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

Recent Progress in Integrated CO2 Capture and Conversion Process Using Dual Function Materials: A State-of-the-Art Review

Mechanochemical synthesis of Ni/MgO dual functional materials at room temperature for CO 2 capture and methanation

Influence of reduction conditions on the structure-activity relationships of NaNO 3 -promoted Ni/MgO dual function materials for integrated CO 2 capture and methanation

MgO promoted by Fe2O3 and nitrate molten salt for fast and enhanced CO2 capture: Experimental and DFT investigation

Material design and prospect of dual-functional materials for integrated carbon dioxide capture and conversion

Efficient CO 2 capture and in-situ electrocatalytic conversion on MgO surface by metal single-atom engineering: A comprehensive DFT study

Integrated CO2 capture and methanation from the intermediate-temperature flue gas on dual functional hybrids of AMS/CaMgO||Ni Co

Synergistic promotions between CO2 capture and in-situ conversion on Ni-CaO composite catalyst

Research progress of metal-organic frameworks-based materials for CO2 capture and CO2-to-alcohols conversion

Dual‐Functional NiMg2−x Ca x Al‐Hydrotalcite for Integrated CO2 Capture and In Situ Methanation

Ni/CaO-based dual-functional materials for calcium-looping CO 2 capture and dry reforming of methane: Progress and challenges

Metal Oxides as Catalyst/Supporter for CO2 Capture and Conversion, Review

Research on CO2 Adsorption Performances of Metal-Doped (ca, Fe and Al) MgO

Two birds with one stone: MgO promoted Ni-CaO as stable and coke-resistant bifunctional materials for integrated CO 2 capture and conversion

Optimizing alkali metal Salt-Induced structural assembly of Ni-MgO dual function materials for enhanced CO 2 capture and methanation performance

Recent advances in computational study and design of MOF catalysts for CO2 conversion

Facile One-Pot Synthesis of Zn/Mg-MOF-74 with Unsaturated Coordination Metal Centers for Efficient CO2 Adsorption and Conversion to Cyclic Carbonates.