Abstract:SrTiO3(STO) is a thermoelectric (TE) material with a wide band gap. It is usually either sintered or annealed in a reducing atmosphere to obtain semiconducting behavior. In this work, non-stoichiometric SrTiO2.8 was synthesized by the high temperature and high pressure (HPHT) method in a reducing environment to obtain improved electrical and thermal properties. The reducing environment was obtained by the application of high pressure and due to the strong ability of Ti to capture oxygen at high temperatures. The thermoelectric properties of the samples synthesized at high temperature and pressure were studied by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and UV spectroscopy. The results show that with increasing of synthesis pressure, the band gap of the samples decreases, improving their electrical properties; at the same time, the high pressure also changes the micro-morphology of the samples and improves their thermal properties. The zT value of the sample synthesized at 5 GPa reached the maximum value of 0.20 at 973 K. It was found that the mechanical strength of the synthesized samples is superior to that of the traditional alloy-based thermoelectric materials. Our work shows that HPHT provides a new variable of pressure for the optimization of the synthesis process of TE materials and provides a new approach for the synthesis and performance optimization of thermoelectric materials.

Study on the properties of Ca9Co12O28 under high pressure

Ultrasonic-assisted Hot Pressing of Bi2Te3-based Thermoelectric Materials

Synthesis and characterization of non -stoichiometric SrTiO2.8 thermoelectric materials at high temperature and high pressure

Microstructure and high temperature electrical properties of AgSbTe2 synthesized by high pressure

High Temperature Thermoelectric Properties of PbTe Prepared by High Pressure Method

Research on Properties of Ca<sub>3-x</sub> La <sub>x</sub>Co<sub>4</sub>O<sub>9</sub> Thermoelectric Material with Adding La

High Pressure Synthesis and Electrical Properties of Ag1-x Pb18 SbTe20

The Thermoelectric Properties of BaxIn0.2−x Co4Sb11.5Te0.5 Synthesized at Different Pressure

Chemical synthesis of Ca9Co12O28 and thermoelectric power

High-Pressure Synthesis of Te-Ge Double-Substituted Skutterudite with Enhanced Thermoelectric Properties

High Pressure Synthesis and Electrical Properties of Ag;Pb;SbTe

The Thermoelectric Properties of Co4Sb12-xTex Synthesized at Different Pressure

High thermoelectric properties of P-SiGe/Sr0.9La0.1Ti0.9-xZrxNb0.1O3 composite

High performance of Bi2Te3-based thermoelectric generator owing to pressure in fabrication process

High Temperature Thermoelectric Properties of Oxide Ca2co2o5

Mechanical, electronic and thermodynamic properties of TE-C36 under high pressure

High Temperature Thermoelectric Properties of Oxide Ca<sub>2</sub>Co<sub>2</sub>O<sub>5</sub>

Enhanced High Temperature Thermoelectric Characteristics Of Transition Metals Doped Ca3co4o9+Delta By Cold High-Pressure Fabrication

Investigating the Thermoelectric Properties of Synthesized Bi2Te3 under Different Synthesis Pressures

Enhanced Thermoelectric Performance in N-Type Bi2te2.95se0.05 Bulks Fabricated by High Pressure Sintering Technique

Preparation of titanium-tantalum-oxygen composite thermoelectric ceramics through high-pressure and high-temperature method