Abstract:Al-Si alloys have been widely used in electronic information, communication and other fields because of their high specific strength, excellent castability and good thermal conductivity. In recent years, with the rapid development of 5G communication technology, electronic communication equipment is gradually developing towards high integration and lightweight. The power of related equipment is higher and higher, which puts forward higher requirements for thermal conductivity and mechanical properties of materials. Si can improve the fluidity and strength of the Al-Si alloy, but a large amount of Si will aggravate the lattice distortion and promote the increase of eutectic Si. This will reduce the plasticity of the alloy, increase the electron scattering and reduce the thermal conductivity. In order to improve the mechanical properties and thermal conductivity of Al-Si alloys, chemical inoculation is generally used. Sr is usually used as modifier and Al-B is as grain refiner. However, the simultaneous addition of Sr and B in Al-Si alloy results in "poisoning" phenomenon, it is impossible to refine α- Al grains and modified eutectic Si simultaneously. In recent years, rare earth La has attracted more and more attention in improving the properties of aluminum alloys. However, previous studies have mainly focused on the effects of La addition, the effects of combined addition of La, Sr, B on the microstructure and properties of Al-7Si-0.6 Fe alloy is lack. In this work, solidification experiments were performed to investigate the effects of combined addition of La, Sr, B on the microstructure and properties of Al-7Si-0.6 Fe alloy. The results show that the addition of trace rare earth La can effectively eliminate the poisoning effect of Sr and B, and enhance the modification effect of eutectic Si. Besides, La addition can promote the formation of α-Al heterogeneous nucleation substrate LaB6 and La can be used as a surfactant to reduce the undercooling of α-Al nucleation, thus it refines α-Al grains. The thermal conductivity of the alloy is significantly improved when the addition of La ranges from 0.02% to 0.06%, with the further increase of La addition, LaAlSi intermetallic compounds are formed in the alloy, leading to a decrease in the thermal conductivity of the alloy.

Influence of minor addition of La and Ce on the ageing precipitation behavior of Sr-modified Al-7Si-0.6Mg alloy

The Influence of the Combined Addition of La–Ce Mixed Rare Earths and Sr on the Microstructure and Mechanical Properties of AlSi10MnMg Alloy

The effects of Ti on the precipitation evolution and age-hardening behavior of Al–7Si–Mg alloy

Influence of Li addition on mechanical property and aging precipitation behavior of Al-3.5Cu-1.5Mg alloy

INFLUENCE OF ADDITIVE Sr OR Sb ON MODIFICATION OF Al-Si ALLOYS

Influence of Mg content on ageing precipitation behavior of Al-Cu-Li-x alloys

Effect of trace rare earth La on microstructure and properties of Al-7Si-0.6 Fe alloy

Effect of Rare Earth Ce Addition on the Microstructure and Mechanical Properties of an Al–Cu–Mg–Ag Alloy

Effect of Si addition on the precipitation and mechanical/electrical properties of dilute Al-Zr-Sc alloys

The Effect of Grain Refinement and Precipitation Strengthening Induced by Sc or Er Alloying on the Mechanical Properties of Cast Al-Li-Cu-Mg Alloys at Elevated Temperatures

Effect of Sr Modification on the Microstructures, Mechanical Properties, and Thermal Conductivity of Hypoeutectic Al-13.6Cu-6Si Alloys

Effect of Addition of La and Ce on Solidification Behavior of Al-Cu Alloys

The influence of La and Ce additions on the solidification of alloys from the Al–Fe system

Effect of Cu addition on precipitation and age-hardening response of an Al-15%Mg2Si alloy

Effect of Ce Content on the Microstructure and Mechanical Properties of Al-Cu-Li Alloy

Effect of Ce/La Microalloying on Microstructural Evolution of Mg-Zn-Ca Alloy During Solution Treatment

Effect of a Trace Addition of Sn on the Aging Behavior of Al–Mg–Si Alloy with a Different Mg/Si Ratio

Effects of La addition on the mechanical properties and thermal-resistant properties of Al–Mg–Si–Zr alloys based on AA 6201

Precipitates evolution and strengthening of Al–Mg2Si alloys containing high-Cu contents during ageing process

Effects of Zr,Ti and Sc Additions on the Microstructure and Mechanical Properties of Al-0.4Cu-0.14Si-0.05Mg-0.2Fe Alloys

Influence of Ce on microstructure and mechanical properties of LA141 alloys