Abstract:Ni-MgO dual function materials (DFMs) show promise for integrated CO2 sorption and methanation. To improve CO2 sorption capacity, Ni-MgO DFMs are promoted with alkali metal nitrates. However, the high catalyst reduction temperature will result in high energy consumption, huge temperature gap between reduction (similar to 650 degrees C) and CO2 sorption and methanation (similar to 300 degrees C), and the loss of alkali metal nitrates. In this work, we prepared a Ni/CeO2 catalyst and investigated the effect of reduction temperature on its structure-property relationships in CO2 methanation, aiming to lower the reduction temperature to an isothermal level that matches CO2 methanation. Results indicated that the reduction temperature fell from over 650 to 300 degrees C, and Ni/CeO2 reduced at 300 degrees C featured high CO2 conversion (72.7%) and CH4 selectivity (98.9%). The CO2 methanation activity of Ni/CeO2 declined significantly when the reduction temperature exceeded 400 degrees C. The formation of more oxygen vacancy defects due to the interaction between NiO and CeO2 promoted the reduction of NiO species at lower temperatures. The declined CO2 methanation activity at high reduction temperatures was ascribed to the consumption of oxygen vacancies in catalyst reduction, and less defects were available for CO2 activation and methanation. An alkali metal nitrate promoted MgO adsorbent was physically mixed with Ni/CeO2 to construct (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs for integrated CO2 sorption and methanation. The DFMs could be facilely reduced at 300 degrees C, and this has made it possible to realize the isothermal operation of catalyst reduction and CO2 sorption and methanation in integrated CO2 capture and utilization (ICCU). The (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs reduced at 300 degrees C exhibited an impressive CO2 uptake of 2.74 mmol CO2/g DFMs and a great CH4 yield of 1.10 mmol CH4/g DFMs, and they could be a promising alternative to Ru-based DFMs with respect to their comparable CO2 sorption capacity and methanation activity and minimized cost of raw materials.

Ni nanoparticles enclosed in highly mesoporous nanofibers with oxygen vacancies for efficient CO2 methanation

Insights into Nickel-Based Dual Function Materials for CO2 Sorption and Methanation: Effect of Reduction Temperature

Abundant interfacial and intrinsic oxygen vacancies enabling small nickel/ceria nanocrystal efficient CO 2 methanation

Metal organic framework derived Ni/CeO2 catalyst with highly dispersed ultra-fine Ni nanoparticles: Impregnation synthesis and the application in CO2 methanation

Highly Stable and Selective Ni/ZrO2 Nanofiber Catalysts for Efficient CO2 Methanation

Ni/CeO2 catalysts for low-temperature CO2 methanation: Identifying effect of support morphology and oxygen vacancy

CO2 Methanation over the Ni-based Catalysts Supported on Nano-Ceo2 with Varied Morphologies

Doping Pd2+ into NinCeOx Nanofibers Promotes Low-Temperature CO2 Methanation

Vacancy engineering of the nickel-based catalysts for enhanced CO<sub>2</sub> methanation

A detailed characterization study of Ni/CeO 2 catalysts identifies Ni availability as the primary factor affecting CO 2 methanation performance

Highly active Ni/CeO2/SiO2 catalyst for low-temperature CO2 methanation: Synergistic effect of small Ni particles and optimal amount of CeO2

Niobium Modification of CeO2 Tuning Electron Density of Nickel-Ceria Interfacial Sites for Enhanced CO2 Methanation

CO2 methanation over Ni nanoparticles inversely loaded with CeO2 and Cr2O3: Catalytic functions of metal oxide/Ni interfaces

Oxygen Vacancy-Dependent Low-Temperature Performance of Ni/CeO2 in CO2 Methanation

Enhancement of hollow Ni/CeO2-Co3O4 for CO2 methanation: From CO2 adsorption and activation by synergistic effects

Facilely Fabricating Highly Dispersed Ni-based Catalysts Supported on Mesoporous MFI Nanosponge for CO2 Methanation

Ceria engineering in nickel catalysts to improve CH 4 selectivity and yield for CO methanation

Highly Stable and Selective Ni/ZrO 2 Nanofiber Catalysts for Efficient CO 2 Methanation

Why Ni/CeO2 is More Active Than Ni/SiO2 for CO2 Methanation? Identifying Effect of Ni Particle Size and Oxygen Vacancy

Effective CO2 Activation of Enriched Oxygen Vacancies for Photothermal CO2 Methanation

Ni-based mesoporous Ce0.8Zr0.2O2 catalyst with enhanced low-temperature performance for CO2 methanation