Abstract:Ni-MgO dual function materials (DFMs) show promise for integrated CO2 sorption and methanation. To improve CO2 sorption capacity, Ni-MgO DFMs are promoted with alkali metal nitrates. However, the high catalyst reduction temperature will result in high energy consumption, huge temperature gap between reduction (similar to 650 degrees C) and CO2 sorption and methanation (similar to 300 degrees C), and the loss of alkali metal nitrates. In this work, we prepared a Ni/CeO2 catalyst and investigated the effect of reduction temperature on its structure-property relationships in CO2 methanation, aiming to lower the reduction temperature to an isothermal level that matches CO2 methanation. Results indicated that the reduction temperature fell from over 650 to 300 degrees C, and Ni/CeO2 reduced at 300 degrees C featured high CO2 conversion (72.7%) and CH4 selectivity (98.9%). The CO2 methanation activity of Ni/CeO2 declined significantly when the reduction temperature exceeded 400 degrees C. The formation of more oxygen vacancy defects due to the interaction between NiO and CeO2 promoted the reduction of NiO species at lower temperatures. The declined CO2 methanation activity at high reduction temperatures was ascribed to the consumption of oxygen vacancies in catalyst reduction, and less defects were available for CO2 activation and methanation. An alkali metal nitrate promoted MgO adsorbent was physically mixed with Ni/CeO2 to construct (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs for integrated CO2 sorption and methanation. The DFMs could be facilely reduced at 300 degrees C, and this has made it possible to realize the isothermal operation of catalyst reduction and CO2 sorption and methanation in integrated CO2 capture and utilization (ICCU). The (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs reduced at 300 degrees C exhibited an impressive CO2 uptake of 2.74 mmol CO2/g DFMs and a great CH4 yield of 1.10 mmol CH4/g DFMs, and they could be a promising alternative to Ru-based DFMs with respect to their comparable CO2 sorption capacity and methanation activity and minimized cost of raw materials.

Frustrated Lewis Pairs Boosting Low-Temperature CO(2 )Methanation Performance over Ni/CeO2 Nanocatalysts

Frustrated Lewis Pairs Boosting Low-Temperature CO<sub>2 </sub>Methanation Performance over Ni/CeO<sub>2</sub> Nanocatalysts

Engineering MOx/Ni Inverse Catalysts for Low-Temperature CO2 Activation with High Methane Yields

Optimizing low-temperature CO2 methanation through frustrated Lewis pairs on Ni/CeO2 catalysts

Insights into Nickel-Based Dual Function Materials for CO2 Sorption and Methanation: Effect of Reduction Temperature

Enhancing the low-temperature CO2 methanation over Ni/La-CeO2 catalyst: The effects of surface oxygen vacancy and basic site on the catalytic performance

Highly active Ni/CeO2/SiO2 catalyst for low-temperature CO2 methanation: Synergistic effect of small Ni particles and optimal amount of CeO2

CO2 Methanation over the Ni-based Catalysts Supported on Nano-Ceo2 with Varied Morphologies

Metal organic framework derived Ni/CeO2 catalyst with highly dispersed ultra-fine Ni nanoparticles: Impregnation synthesis and the application in CO2 methanation

Ni/CeO2 catalysts for low-temperature CO2 methanation: Identifying effect of support morphology and oxygen vacancy

Boosting Low-Temperature CO2 Hydrogenation over Ni-based Catalysts by Tuning Strong Metal-Support Interactions.

The structure activity relationship of promoted La doped Ni-CeO 2 catalysts prepared by continuous-flow microreactor for low temperature CO 2 methanation

Highly Stable and Selective Ni/ZrO2 Nanofiber Catalysts for Efficient CO2 Methanation

The Structure Activity Relationship of Promoted La Doped Ni-CeO2 Catalysts Prepared by Continuous-Flow Microreactor for Low Temperature CO2 Methanation

Eu3+ Doping-Promoted Ni-CeO2 Interaction for Efficient Low-Temperature CO2 Methanation

CO2 methanation over Ni nanoparticles inversely loaded with CeO2 and Cr2O3: Catalytic functions of metal oxide/Ni interfaces

Enhanced low-temperature CO2 methanation performance of Ni/ZrO2 catalysts via a phase engineering strategy

Fabrication of Surface Oxygen Vacancies on NiMnAl-LDO Catalyst by High-Shear Mixer-Assisted Preparation for Low-Temperature CO2 Methanation

CO2 Methanation on the Catalyst of Ni/MCM-41 Promoted with CeO2

Boosting CO2 Methanation Via Tuning Metal-Support Interaction over Hollow Ni/CeO2

Unveiling the Synergistic Role of Frustrated Lewis Pairs in Carbon‐Encapsulated Ni/NiOx Photothermal Cocatalyst for Enhanced Photocatalytic Hydrogen Production