Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Very high-cycle fatigue performance of high carbon-chromium bearing steels with different metallurgical qualities

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Fatigue behavior of GCr15 steel in ultra-high life region

Reliability evaluation on very high cycle fatigue property of GCr15 bearing steel

2025 Very High Cycle Fatigue Behavior of High Carbon Chromium Bearing Steel, Gcr15

Fatigue Behavior of GCrl5 Steel in Ultra-High Life Region

Correlations Between Very High Cycle Fatigue Properties and Inclusions of Gcr15 Bearing Steel

Experimental Investigation on Low Cycle Fatigue Properties of GH3536 Alloy with Film Cooling Holes in Different Drilling Processes

Very High Cycle Fatigue for GCr15 Steel with Smooth and Hole-Defect Specimens

Current Status of Metallurgical Quality and Fatigue Performance of Rolling Bearing Steel and Development Direction of High-End Bearing Steel

Effects of heat treatment on fatigue properties of double vacuum smelting high‐carbon chromium bearing steel

Distinguishing effect of turning and grinding on the surface integrity and fatigue performance of ultra-high strength steel

Effects of Strength Level and Loading Frequency on Very-High-Cycle Fatigue Behavior for A Bearing Steel

Fatigue Crack Initiation and Propagation at High Temperature of New-Generation Bearing Steel

Effects of Double Quenching on Fatigue Properties of High Carbon Bearing Steel with Extra-High Purity

High/very-high Fatigue Properties and Microstructure Evolutions of 9cr3w3co Turbine Rotor Steel at Room Temperature and 650 °C

Roles of microstructures in high-cycle fatigue behaviors of 42CrMo high-strength steel under near-yield mean stress

Fatigue and recrystallization evolution of carbide-free bainitic layer under high-stress rolling sliding contact

High-temperature fatigue behavior and cyclic deformation of a gradient nanostructured RAFM steel

Very-High-Cycle Fatigue Behaviors for Bearing Steel Microstructural Transformation

Very High Cycle Fatigue Behavior of SAE52100 Bearing Steel by Ultrasonic Nanocrystalline Surface Modification