Self-healing performance and corrosion resistance of novel CeO2-sealed MAO film on aluminum alloy

Yue Gong,Jiwei Geng,Jie Huang,Zhe Chen,Mingliang Wang,Dong Chen,Haowei Wang

DOI: https://doi.org/10.1016/j.surfcoat.2021.127208

IF: 4.865

2021-07-01

Surface and Coatings Technology

Abstract:<p>The self-healing performance with the improved corrosion resistance of novel CeO₂-sealed micro-arc oxide (MAO) film on Al alloy was studied in this work for the first time. There are three steps involved, including: (1) Preparing porous film by performing MAO treatment on Al alloy with the average thickness of ~15 μm; (2) loading corrosion inhibitor by soaking MAO sample in Ce(NO₃)₃ solution to fulfill micropores-sealing process; (3) evaluating the self-healing ability of the sealed MAO film in acidic, alkaline and neutral solutions by scratch tests. The experimental results indicated that the corrosion inhibitor was characterized to be CeO₂ which can locally fill the micropores to seal the MAO film. The optimized CeO₂-sealed MAO film owned the lower porosity and the improved the corrosion resistance, which can be testified from the corrosion current density (<em>I</em>_{<em>corr</em>}) decreased by 2 orders of magnitude compared with the MAO film. Furthermore, the micropores in the MAO film acted as microcontainers to hold corrosion inhibitor to make CeO₂-sealed MAO film showed self-healing ability. In the acidic environment (pH = 2 (8 mL/L H₂SO₄ + 20 mL/L H₂O₂)), the novel CeO₂-sealed film exhibited positive self-healing effect morphologically with improved corrosion test result, and the underlying self-healing mechanism was discussed in detail.</p>

physics, applied,materials science, coatings & films

What problem does this paper attempt to address?

The paper primarily aims to address the issue of localized corrosion in aluminum alloys caused by surface film damage in practical applications. Specifically, the research team prepared a porous film on the surface of aluminum alloys using Micro-Arc Oxidation (MAO) technology and further filled these porous structures with Ce(NO3)3 solution to form a self-healing film. The specific problems the paper attempts to solve are as follows:

1. **Enhancing the corrosion resistance of aluminum alloys**:
- Although aluminum alloys have advantages such as light weight and high strength, their high chemical activity and poor corrosion resistance limit their widespread application.
- Researchers hope to improve the corrosion resistance of aluminum alloys by enhancing surface treatment techniques.

2. **Achieving self-healing functionality**:
- When the surface film of aluminum alloys is damaged, traditional methods cannot effectively prevent the occurrence and spread of corrosion.
- This study aims to introduce self-healing materials so that damaged areas can automatically repair themselves, preventing further development of corrosion.

3. **Finding new methods to replace chromate**:
- Traditional chromate conversion coatings have good self-healing capabilities but have been banned due to their toxicity.
- Researchers explored new corrosion inhibitors based on cerium compounds to replace toxic chromates.

4. **Optimizing the performance of self-healing films**:
- By adjusting the immersion time and process parameters, the study seeks the best preparation scheme for self-healing films.
- Evaluating the effectiveness of self-healing films in different environments (acidic, alkaline, and neutral).

Through the above research, the paper not only verifies that CeO2-sealed MAO films significantly enhance corrosion resistance but also demonstrates positive self-healing effects in acidic environments and discusses the self-healing mechanism in detail.