Amino-Modified Graphene Oxide from Kish Graphite for Enhancing Corrosion Resistance of Waterborne Epoxy Coatings

Shengle Hao,Siming Wan,Shiyu Hou,Bowen Yuan,Chenhui Luan,Ding Nan,Gen Huang,Deping Xu,Zheng-Hong Huang

DOI: https://doi.org/10.3390/ma17051220

IF: 3.4

2024-03-07

Materials

Abstract:Waterborne epoxy (WEP) coatings with enhanced corrosion resistance were prepared using graphene oxide (GO) that was obtained from kish graphite, and amino-functionalized graphene oxide (AGO) was modified by 2-aminomalonamide. The structural characteristics of the GO and AGO were analyzed using X-ray diffraction (XRD), Raman spectroscopy, Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). And the anti-corrosive performance of waterborne epoxy-cased composite coatings with different addition amounts of AGO was investigated using electrochemical measurements, pull-off adhesion tests, and salt spray tests. The results indicate that AGO15/WEP with 0.15 wt.% of AGO has the best anti-corrosive performance, and the lowest frequency impedance modulus increased from 1.03 × 108 to 1.63 × 1010 ohm·cm−2 compared to that of WEP. Furthermore, AGO15/WEP also demonstrates the minimal corrosion products or bubbles in the salt spray test for 200 h, affirming its exceptional long-term corrosion protection capability.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem this paper attempts to address is improving the anti-corrosion performance of waterborne epoxy resin (WEP) coatings. Specifically, the authors prepared graphene oxide (GO) from kish graphite and further modified it with 2-aminomalonamide to produce amino-modified graphene oxide (AGO). Different amounts of AGO were then added to WEP to enhance its anti-corrosion performance. The main objectives of the study are:

1. **Improve anti-corrosion performance**: Enhance the anti-corrosion ability of WEP coatings by adding AGO, particularly targeting the formation of micropores and microcracks, which can affect the barrier performance of the coating and reduce its service life.
2. **Optimize AGO content**: Determine the optimal amount of AGO to be added to achieve the best anti-corrosion effect.
3. **Verify long-term anti-corrosion capability**: Evaluate the long-term anti-corrosion performance of the composite coating through electrochemical measurements, peel adhesion tests, and salt spray tests.

Overall, the study aims to develop a cost-effective and environmentally friendly anti-corrosion measure to meet industrial needs and reduce the risk of metal corrosion.