Abstract:In this paper, the local corrosion inhibition effect of imidazoline on N80 oil pipeline steel in a NaCl-Na2S solution was studied by the simulated blocking tank cell method, and the corrosion processes of the cathode and anode in the blocking zone were simulated. The blocking corrosion behavior of the pipeline tubing steel N80 in simulated corrosion solutions without and with different concentrations of an imidazoline corrosion inhibitor was studied by chemical analysis and electrochemical analysis. The results show that in the three solution systems, after the anode polarization of the occluded cell, the solution in the occluded region is acidified, the pH value decreases sharply, the migration of Cl− and S2− increases, and the concentration is increased in the blocked area. After adding the imidazoline corrosion inhibitor, the imidazoline inhibitor can reduce the migration of small-radius anions (Cl− and S2−) to the occluded area, inhibit the acidification of the solution in the occluded area, and prevent the dissolution of metals in the occluded area. As a result, the corrosion of the occluded area is slowed down due to the change in the chemical and electrochemical state of the occluded area. In the three corrosion solution systems of 2% Na2S + 5% NaCl, 2% Na2S + 8% NaCl, and 2% Na2S + 10% NaCl, the imidazoline corrosion inhibitor can form an adsorption film on the metal surface, thereby increasing the polarization resistance and decreasing the corrosion rate. The addition of an imidazoline corrosion inhibitor can significantly increase the kinetic constant of anode polarization, which can effectively inhibit the local corrosion of N80 steel in these corrosion systems.

What problem does this paper attempt to address?

The problem this paper attempts to address is: the inhibition of localized corrosion of N80 petroleum pipeline steel in NaCl-Na2S solution using imidazoline quaternary ammonium salt inhibitors. Specifically, the researchers studied the effect of imidazoline on the localized corrosion inhibition of N80 tubing steel in NaCl-Na2S solution through a simulated closed-cell method, and simulated the cathodic and anodic corrosion processes within the closed area. The study explored the impact of different concentrations of imidazoline corrosion inhibitors on the closed corrosion behavior of N80 steel pipes in simulated corrosive solutions through chemical and electrochemical analysis methods. The study found that in three solution systems (2% Na2S + 5% NaCl, 2% Na2S + 8% NaCl, 2% Na2S + 10% NaCl), the addition of imidazoline corrosion inhibitors can reduce the migration of small radius anions (Cl− and S2−) into the closed area, inhibit the acidification of the solution within the closed area, and prevent the dissolution of metal in the closed area, thereby slowing down the corrosion in the closed area. Imidazoline corrosion inhibitors can also form an adsorption film on the metal surface, increase polarization resistance, reduce the corrosion rate, significantly improve the kinetic constants of anodic polarization, and effectively inhibit the localized corrosion of N80 steel in these corrosive systems.

Inhibition Localized Corrosion of N80 Petroleum Pipeline Steel in NaCl-Na2S Solution Using an Imidazoline Quaternary Ammonium Salt

Experimental and Theoretical Investigation of 1-Hexyl-3-methylimidazolium Iodide As a Corrosion Inhibitor for Mild Steel in HCl Environment

Corrosion Inhibition Behavior of X80 Pipeline Steel by Imidazoline Derivative in the CO2-saturated Seawater Containing Sulfate-Reducing Bacteria with Organic Carbon Starvation

Inhibition of the Corrosion of X70 and Q235 Steel in CO2-saturated Brine by Imidazoline-Based Inhibitor

Preparation and Inhibition Performance of Aryl-Imidazoline Quaternary-Ammonium-salt Corrosion Inhibitor

Evaluation of Inhibition Efficiency of an Imidazoline Derivative in CO2-containing Aqueous Solution

Study of the inhibition mechanism of imidazoline derivative inhibitor on CO2 corrosion for Q235 steel

Corrosion Inhibition Effect of N-(4-diethylaminobenzyl) Quaternary Ammonium Chitosan for X80 Pipeline Steel in Hydrochloric Acid Solution

Corrosion Inhibition of A3 Steel by Imidazoline Derivative in 2·0%nacl Solution

Research on the Inhibition Behavior of Imidazoline Derivant in the Oil/Gas Well Containing H2 S/CO2

Effectiveness of an amine-based inhibitor—guanidine for steel in chloride-contaminated concrete

Experimental and theoretical investigations of a novel imidazoline quaternary ammonium salt as an effective inhibitor of Q235 steel in 1 M HCl

Imidazoline behavior as corrosion inhibitor in the electrochemical characterization of SCC behavior of an API X70 steel exposed to brine solution

Theoretical and Experimental Studies for Corrosion Inhibition Performance of Q235 Steel by Imidazoline Inhibitors Against CO2 Corrosion

Corrosion Inhibition Properties of Corrosion Inhibitors to under-Deposit Corrosion of X65 Steel in CO2 Corrosion Conditions

The Behavior of Pre-Corrosion Effect on the Performance of Imidazoline-Based Inhibitor in 3 Wt.% NaCl Solution Saturated with CO2

Electrochemical Research on Inhibition Mechanism of Thiazole in Gas or Oil Field

Microscopic Influence Mechanisms of Polysaccharide on the Adsorption and Corrosion Inhibition Performance of Imidazoline on Metal Surface

A New Imidazole Derivative for Corrosion Inhibition of Q235 Carbon Steel in an Acid Environment

Molecular Dynamic Simulation and Experimental Investigation on the Synergistic Mechanism and Synergistic Effect of Oleic Acid Imidazoline and L-Cysteine Corrosion Inhibitors