Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Effect of ionic liquids on the corrosion behaviour of X80 pipeline steel

Experimental and Theoretical Investigation of 1-Hexyl-3-methylimidazolium Iodide As a Corrosion Inhibitor for Mild Steel in HCl Environment

Corrosion Inhibition Properties of Corrosion Inhibitors to under-Deposit Corrosion of X65 Steel in CO2 Corrosion Conditions

Effect and mechanism of ionic liquid-polymer composite coating on enhancing hydrogen embrittlement resistance of X80 pipeline steel for hydrogen blended natural gas transportation

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Effect of interaction between corrosion film and H2S/CO2 partial pressure ratio on the hydrogen permeation in X80 pipeline steel

Corrosion Inhibition Effect of N-(4-diethylaminobenzyl) Quaternary Ammonium Chitosan for X80 Pipeline Steel in Hydrochloric Acid Solution

Revealing the Deterioration Effect of Scale Inhibitor on the Performance of Corrosion Inhibitor under Dynamic Conditions

Inhibiting Effect of Ionic Liquids on the Corrosion of Mild Steel in H2S and HCl Solution

Experimental and computational studies of novel cyclic ammonium based ionic liquids as corrosion inhibitors for carbon steel in acid medium

Temperature Effect on the Corrosion Inhibition of Carbon Steel by Polymeric Ionic Liquids in Acid Medium

Inhibition Localized Corrosion of N80 Petroleum Pipeline Steel in NaCl-Na2S Solution Using an Imidazoline Quaternary Ammonium Salt

Effects of La3+ on the Hydrogen Permeation and Evolution Kinetics in X70 Pipeline Steel

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments

Bio-based ionic liquid as a corrosion inhibitor for mild steel in 5% HCl solution: Experimental and theoretical investigation

Adsorption, thermodynamic, and quantum chemical investigations of an ionic liquid that inhibits corrosion of carbon steel in chloride solutions

Corrosion Inhibition of X100 Pipeline Steel in 1 M HCl by Two Complexes of Cystine

Study on corrosion inhibitor in large pipelines under multiphase flow using EIS

The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements

Evaluation of ionic liquids based imidazolium salts as an environmentally friendly corrosion inhibitors for carbon steel in HCl solutions

Study on corrosion inhibitor technology in gas pipeline