Utilization of ground granulated blast-furnace slag and electrolytic manganese residue as a low-carbon cementitious material
Chaoliu Tu,Lei Lang,Xiaohan Nie,Yong Yang,Lei Liu,Wang Ping,Jiangshan Li,Chaoliu TuLei LangXiaohan NieYong YangLei LiuWang PingJiangshan Lia State Key Laboratory of Geomechanics and Geotechnical Engineering,Institute of Rock and Soil Mechanics,Chinese Academy of Sciences,Wuhan,Chinab University of Chinese Academy of Sciences,Beijing,Chinac Hubei Province Key Laboratory of Contaminated Sludge and Soil Science and Engineering,Wuhan,Chinad IRSM-CAS/HK PolyU Joint Laboratory on Solid Waste Science,Wuhan,Chinae School of Urban Construction,Wuhan University of Science and Technology,Wuhan,Chinaf Beijing Water Science and Technology Institute,Beijing,China
DOI: https://doi.org/10.1080/21650373.2023.2281628
2023-11-25
Journal of Sustainable Cement-Based Materials
Abstract:Ground granulated blast-furnace slag (GGBS) is a common substitute for ordinary Portland cement (OPC). However, GGBS–OPC lacks early strength when OPC content is low (<50%). A new cementitious material called GGBS–OPC–EMR (GOE) was developed by adding electrolytic manganese residue (EMR) to address this issue. Tests were conducted using XRD, SEM, and TG to analyze the micro-structural mechanisms of strength development in GOE. Environmental and economic evaluations were conducted, including CO 2 -eq (carbon dioxide equivalent) analysis, leaching tests, and economic analysis. Results showed that mixture of GGBS, OPC, and EMR in a 4:2:1 ratio increased the unconfined compressive strength by 25% after 28 days compared to OPC while reducing cement consumption by 70%. Major hydration products in GOE were C–S–H and ettringite (AFt), with approximately 14% EMR promoting AFt production. GOE reduced CO 2 -eq emissions by 35.9% and saved $46.6/ton compared to OPC. Leaching tests demonstrated GOE's ability to stabilize heavy metals, sulfate, and ammonia nitrogen.
construction & building technology,materials science, multidisciplinary,green & sustainable science & technology