Abstract:The global need to reduce carbon dioxide (CO 2 ) emissions prompted studies on sustainable alternatives to conventional concrete made with ordinary Portland cement (OPC) binders. Alkali-activated ground granulated blast furnace slag (GGBS) is a promising sustainable to OPC in terms of the impact on the environment and reduction of CO 2 emissions. Concretes and mortars made with alkali-activated binders demonstrate promising fresh and mechanical properties. This article presents the findings of an experimental study investigating the fresh and mechanical properties of mortar using alkali-activated GGBS binder. The activators used were sodium silicate (Na 2 SiO 3 ) and sodium hydroxide (NaOH) solution with 6 M, 8 M, 10 M, and 12 M molarities. The study assessed their initial setting time, workability, and 28-day compressive strength. The study evaluated the effect of partial replacement of GGBS with 5 % silica fume. The compressive strength was determined after 28 days of curing in three different environments: 1) ambient air temperature, 2) water submersion, and 3) water immersion for 7 days followed by 21 air curing in ambient temperature. The results showed an increase in compressive strength with higher NaOH concentration but a corresponding decrease in initial setting time and flowability. Depending on the curing method, efflorescence, and blue-green pigmentation were seen during the physical assessment of the samples. The highest 28-day compressive strength was 67.5 MPa when the NaOH activator molarity was 10 mol/L which represents an optimum concentration for strength development. Replacing 5 % of the GGBS binder with silica fume resulted in a decrease in the 28-day compressive strength and workability without affecting the initial setting time.

Incorporation of reactive magnesia and quicklime in sustainable binders for soil stabilisation

Initial Investigation of Soil Stabilization with Calcined Dolomite-GGBS Blends

Comparison between CaO- and MgO-activated ground granulated blast-furnace slag (GGBS) for stabilization/solidification of Zn-contaminated clay slurry

Comparison of Mechanical Properties of the Geopolymer-Solidified Soils Activated by Two Alkaline Oxides

Deep insight into mechanical behavior and microstructure mechanism of quicklime-activated ground granulated blast-furnace slag pastes

Study of durability of reactive magnesia-activated ground granulated blast-furnace slag stabilized soil attacked by sulfate sodium solution

Alkali-Activated Ground-Granulated Blast Furnace Slag for Stabilization of Marine Soft Clay

Stabilization of a Clay Soil Using Cementing Material from Spent Refractories and Ground-Granulated Blast Furnace Slag

Three-year Performance of In-Situ Solidified/stabilised Soil Using Novel MgO-bearing Binders.

Research on Alkali-Activated Slag Stabilization of Dredged Silt Based on a Response Surface Method

Mechanical and Hydration Properties of Ground Granulated Blastfurnace Slag Pastes Activated with MgO–CaO Mixtures

Strength and hydration properties of reactive MgO-activated ground granulated blastfurnace slag paste

Performance Evaluation of Stabilised/Solidified Contaminated Model Soil Using PC-Based and MgO-Based Binders

Magnesia reactivity on activating efficacy for ground granulated blastfurnace slag for soft clay stabilisation

MgO-GGBS Binder–Stabilized/Solidified PAE-Contaminated Soil: Strength and Leachability in Early Stage

Rheology, Mechanical Properties, and Hydration of Synergistically Activated Coal Gasification Slag with Three Typical Solid Wastes

Validating the Use of Slag Binder with 91 Percent Blast Furnace Slag for Mine Backfilling

The Performance of Blended Conventional and Novel Binders in the In-Situ Stabilisation/solidification of a Contaminated Site Soil.

Designing Low-Carbon Cement-Free Binders for Stabilization/solidification of MSWI Fly Ash

Effect of activator concentration on setting time, workability and compressive strength of sustainable concrete with alkali-activated slag binder

Strength evolutions of varying water content-dredged sludge stabilized with alkali-activated ground granulated blast-furnace slag