Effects of size on the mechanical response of metallic glasses investigated through in situ TEM bending and compression experiments

C.Q. Chen,Y.T. Pei,J.T.M. De Hosson
DOI: https://doi.org/10.1016/j.actamat.2009.08.070
IF: 9.4
2010-01-01
Acta Materialia
Abstract:Quantitative bending and compression tests on micropillars made of two different amorphous alloys, with tip diameters ranging from 93 to 645nm, are performed in situ in a transmission electron microscope (TEM). Under microcompression each pillar shows an intermittent plastic flow accommodated by inhomogeneous shear banding. However, the individual shear banding events are strongly size-dependent, i.e. in larger pillars the deformation is controlled by nucleation of shear bands, but in smaller pillars it becomes propagation-controlled. On the other hand, the yield stress is essentially size-independent. Microbending tests show further advantages by amplifying size effects and minimizing artifacts. An interesting finding is that by microbending, a switch from highly inhomogeneous to fully homogeneous deformation is observed at an experimentally accessible size regime near 200nm, whereas it is not accessible under microcompression, even at a sub-100nm scale. These size effects are well interpreted by a micromechanical model, leading to a deformation map in the stress-size space. A physical picture of nanoscale shear localization process is also provided.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?