Abstract:This study demonstrates the successful fabrication of near-full density monophasic tetragonal 1.5-mol% yttria-stabilized zirconia (1.5YSZ) ceramics using current-ramp flash (CRF) sintering technique. The process involved regulating Joule heating in the samples by fine-tuning the input power through an alternating current field (nominal current density: 50 mA·mm −2 ) within a 3-minute timeframe at a furnace temperature of 1100°C. This approach effectively enhanced grain size uniformity, which is crucial for preventing sample cracking associated with spontaneous tetragonal-to-monoclinic (T→M) phase transformation, thereby promoting densification with average relative densities exceeding 99%. The highest average fracture toughness of the 1.5YSZ samples was measured at 9.2 MPa·m 0.5 using the standardized single-edge pre-cracked beam method. This toughness is approximately double that of commonly used 3YSZ samples produced by CRF sintering, all of which exhibited comparable average grain sizes and relative densities. Additionally, the 1.5YSZ samples demonstrated nearly identical resistance to low-temperature degradation (LTD) compared to the 3YSZ samples after accelerated hydrothermal aging at 140°C for 15 hours, roughly equivalent to 60 years at 37°C. The reduced yttria concentration in 1.5YSZ facilitates T→M phase transformation at lower stress thresholds, enhancing toughness through increased crack shielding from a larger volume fraction of transformed grains. Furthermore, the uniform yttria distribution in 1.5YSZ, revealed by scanning transmission electron microscopy, compensates for the reduced tetragonal phase stability and contributes to improved LTD resistance. Notably, these exceptional properties were achieved at a furnace temperature 300°C lower and with a sintering duration several hours shorter than those of conventionally-sintered counterparts.

Two‐step reactive flash sintering of high entropy pyrochlore: Densification, grain growth, and microstructural homogeneity

Ultrafast densification of high-entropy oxide (La0.2Nd0.2Sm0.2Eu0.2Gd0.2)2Zr2O7 by reactive flash sintering

Preparation of Gd2Zr2O7 nanoceramics by flash sintering and two-step flash sintering

Formation of single-phase multicomponent zirconate with colossal atomic radius difference via reactive flash sintering

Grain-refining fabrication of nanocrystalline (La0.2Nd0.2Sm0.2Gd0.2Eu0.2)2Zr2O7 high-entropy ceramics by ultra-high pressure sintering

Phase evolution during conventional and reactive flash sintering of (Mg,Ni,Co,Cu,Zn)O via in situ X‐ray diffraction

Self-propagating high-temperature synthesis of ZrO2 incorporated Gd2Ti2O7 pyrochlore

Pressureless Two-Step Sintering of Ultrafine-Grained Tungsten

Fabrication and characterization of high entropy pyrochlore ceramics

Ultra-fast high-temperature sintering (UHS) of Ce0.2Zr0.2Y0.2Gd0.2La0.2O2−δ fluorite-structured entropy-stabilized oxide (F-ESO)

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Pressureless Two-Step Sintering of Ultrafine-Grained Refractory Metals: Tungsten-rhenium and Molybdenum

Single-phase Rare-Earth High-Entropy Zirconates with Superior Thermal and Mechanical Properties

Preparation and effect of grain size on the thermal stability, phase transition, mechanical property, and photocatalytic property of pyrochlore (La0.2Nd0.2Sm0.2Gd0.2Y0.2)2Zr2O7 high-entropy oxide

Realizing near-full density monophasic tetragonal 1.5-mol% yttria-stabilized zirconia ceramics via current-ramp flash sintering

Inhibition of hotspot formation by alumina addition in flash sintering of (La0.2Nd0.2Sm0.2Eu0.2Gd0.2)2Zr2O7 high-entropy ceramic

Reactive flash sintering of TiZrN and TiAlN ternary metal nitrides

Fast densification of dense nano-grained Gd2Zr2O7 ceramic prepared by two-step microwave sintering

Two‐Step Sintering of Ceramics with Constant Grain‐Size, II: BaTiO3 and Ni–Cu–Zn Ferrite

Effect of components on the microstructures and properties of rare-earth zirconate ceramics prepared by ultrafast high-throughput sintering

The impact of flash sintering on densification and plasticity of strontium titanate: High heating rates, dislocation nucleation and plastic flow