Abstract:Nowadays, waste plastics made a significant environmental problems. Chemical converting of the polymers to valuable liquids is a promising method to solve the problem and make excellent benefit. This study investigates the utilization of kaolin, a natural resource, for synthesizing zeolite Na-A and significance of the catalyst crystallinity on the catalytic cracking of a 50:50 mixture of polystyrene (PS) and low-density polyethylene (LDPE). This research aims to identify the optimal hydrothermal conditions for producing crystalline zeolite Na-A and evaluate the effect of crystallinity of synthesized zeolite Na-A on production of liquids. A central composite design (CCD) model is employed to achieve this, selecting three independent variables: hydrothermal temperature (80, 85, 90, 95 and 100 °C), the molarity of the alkaline solution (NaOH concentration = 1,2,3,4 and 5 molar), and hydrothermal time (8, 10.43, 14, 17.56 and 20 h). Fourier transform infrared spectroscopy (FTIR) determines the functional groups which proves the presence of sodium aluminosilicate in the synthesized zeolite. The crystallinity of the produced zeolite Na-A is evaluated through X-ray diffraction (XRD) analysis, optimizing the results using the CCD model. Scanning electron microscopy (SEM) reveals well-formed cubic crystalline structures of zeolite Na-A. The optimum conditions for polymer cracking are determined as hydrothermal temperature of 89 °C, a hydrothermal time of 13 h, and a NaOH molarity of 2.8, while predicted liquid production was obtained 81%. The analysis of ANOVA indicates that the designed model based on CCD calculations is valid for prediction of the process. Finally, gas chromatography with flame ionization detection (GC-FID) is employed to characterize the main resulting value-added components (styrene, toluene, and ethylbenzene) under optimum conditions.

Constrained and Open Mesoporosity in Polypropylene Cracking: Insight From Spectroscopic Investigations of Acidity, Diffusion, and Activity

Opening up ZSM-5 Hierarchical Zeolite's Porosity through Sequential Treatments for Improved Low-Density Polyethylene Cracking

Synthesis and Physicochemical Characterization of Hierarchical ZSM-5: Effect of Organosilanes on the Catalyst Properties and Performance in the Catalytic Fast Pyrolysis of Biomass

Elucidating the structure-performance relationship of typical commercial zeolites in catalytic cracking of low-density polyethylene

Effects of post treatment of HZSM-5 zeolites on catalytic cracking of butene

Unraveling the Role of Mesoporosity and Acidity of Hierarchical Aggregated HZSM-5 in HDPE Vapor Catalytic Cracking for Value-Added Hydrocarbons

Mesoporous Mordenites Obtained by Desilication: Mechanistic Considerations and Evaluation in Catalytic Oligomerization of Pentene

Tuning High-Density Polyethylene Hydrocracking through Mordenite Zeolite Crystal Engineering

Direct Observation Of The Mesopores In Zsm-5 Zeolites With Hierarchical Porous Structures By Laser-Hyperpolarized Xe-129 Nmr

Hierarchical Mordenite Dedicated to the Fluid Catalytic Cracking Process: Catalytic Performance Regarding Textural and Acidic Properties

External Acidity as Performance Descriptor in Polyolefin Cracking using Zeolite-Based Materials

Optimization and Study of the Response Surface of Properties for the Synthesis of ZSM-5 Zeolites with Hierarchical Pore Structure Obtained by Desilication

Probing The Porosity Of Cocrystallized Mcm-49/Zsm-35 Zeolites By Hyperpolarized Xe-129 Nmr

Catalytic Cracking of Polystyrene and Low-Density Polyethylene over Synthesized Zeolite Na-A with Optimized Crystallinity

Catalytic Pyrolysis of Polyethylene with Microporous and Mesoporous Materials: Assessing Performance and Mechanistic Understanding

Exploring the effect of Brønsted acidity of MFI-type zeolites on catalytic cracking temperature of low density polyethylene

Creating Intraparticle Mesopores Inside ZSM-5 Nanocrystals under OSDA-free Conditions and Achievement of High Activity in LDPE Degradation

Facile synthesis of hierarchical porous ZSM-5 zeolite with tunable mesostructure and its application in catalytic cracking of LDPE

Mechanism Investigation of Acid-Tailored USY Zeolites Via Ion Exchange in Polypropylene Cracking

Nano-crystallite Oriented Self-Assembled ZSM-5 Zeolite and Its LDPE Cracking Properties: Effects of Accessibility and Strength of Acid Sites

Selective staining of Brønsted acidity in zeolite ZSM-5-based catalyst extrudates using thiophene as a probe