Abstract:Plastic pollution is a critical environmental issue due to the widespread use of plastic materials and their long degradation time. Hydrocracking (HDC) offers a promising solution to manage plastic waste by converting it into valuable products, namely chemicals or fuels. This work aims to investigates the effect of catalyst accessibility and acidity on the HDC reaction of high density polyethylene (HDPE). Therefore, a variety of materials with significant differences in both textural and acidic properties were tested as catalysts. These include H-USY and H-ZSM.5 zeolites with various Si/Al molar ratios (H-USY: Si/Al = 2.9, 15, 30 and 40; H-ZSM-5: Si/Al = 11.5, 40, 500) and mesostructured MCM-41 materials modified with Ga and Al, also with different Si/metal ratios (Si/Al = 16 and 30; Si/Ga = 63 and 82). Thermogravimetric analysis under hydrogen atmosphere was used as a preliminary screening tool to evaluate the potential of the various catalysts for this application in terms of energy requirements. In addition, batch autoclave reactor experiments (T = 300 °C, PH2 = 20 bar, t = 60 min) were conducted to obtain further information on conversion, product yields and product distribution for the most promising systems. The results show that the catalytic performance in HDPE hydrocracking is determined by a balance between the acidity of the catalyst and its structural accessibility. Accordingly, for catalyst series where the structural and textural properties do not vary with the Si/Al ratio, there is a clear correlation of the HDPE degradation temperature and of the HDPE conversion with the Si/metal ratio (which relates to the acidic properties). In contrast, for catalyst series where the structural and textural properties vary with the Si/Al ratio, no consistent trend is observed and the catalytic performance is determined by a balance between the acidic and textural properties. The product distribution was also found to be influenced by the physical and chemical properties of the catalyst. Catalysts with strong acidity and smaller pores were observed to favor the formation of lighter hydrocarbons. In addition to the textural and acidic properties of the catalyst, the role of coke formation should not be neglected to ensure a comprehensive analysis of the catalytic performance.

Tuning High-Density Polyethylene Hydrocracking through Mordenite Zeolite Crystal Engineering

Mechanistic Understanding of Efficient Polyethylene Hydrocracking over Two-Dimensional Platinum-Anchored Tungsten Trioxide.

Opening up ZSM-5 Hierarchical Zeolite's Porosity through Sequential Treatments for Improved Low-Density Polyethylene Cracking

Hierarchical Mordenite Dedicated to the Fluid Catalytic Cracking Process: Catalytic Performance Regarding Textural and Acidic Properties

Enhanced hydroconversion of polyethylene via dual-functional catalysis: Exploiting ZSM-22 pore-mouth catalysis and Ru electronic effect

Catalyzing the Hydrocracking of Low Density Polyethylene

Unraveling the Role of Mesoporosity and Acidity of Hierarchical Aggregated HZSM-5 in HDPE Vapor Catalytic Cracking for Value-Added Hydrocarbons

Effect of Hierarchical ZSM-5 Zeolite Crystal Size on Diffusion and Catalytic Performance of N-Heptane Cracking

Catalytic Cracking of Polystyrene and Low-Density Polyethylene over Synthesized Zeolite Na-A with Optimized Crystallinity

Constrained and Open Mesoporosity in Polypropylene Cracking: Insight From Spectroscopic Investigations of Acidity, Diffusion, and Activity

Zeolite domination in coordination between metal and acid sites on an industrial catalyst for tetralin hydrocracking

Catalytic pyrolysis of high-density polyethylene (HDPE) over hierarchical ZSM-5 zeolites produced by microwave-assisted chelation-alkaline treatment

Elucidating the structure-performance relationship of typical commercial zeolites in catalytic cracking of low-density polyethylene

Generating TON Zeolites with Reduced [001] Length Through Combined Mechanochemical Bead-Milling and Porogen-Directed Recrystallization with Enhanced Catalytic Property in Hydroisomerization

Single pot catalyst strategy to branched products via adhesive isomerization and hydrocracking of polyethylene over platinum tungstated zirconia

External Acidity as Performance Descriptor in Polyolefin Cracking using Zeolite-Based Materials

Synergetic Regulation of the Microstructure and Acidity of HZSM-5/MCM-41 for Efficient Catalytic Cracking of n-Decane

Effect of Zeolite-Y Modification on Crude-Oil Direct Hydrocracking

Conversion of polyethylene waste to short chain hydrocarbons under mild temperature and hydrogen pressure with metal-free and metal-loaded MFI zeolites

Exploring the effect of Brønsted acidity of MFI-type zeolites on catalytic cracking temperature of low density polyethylene

Catalyst Accessibility and Acidity in the Hydrocracking of HDPE: A Comparative Study of H-USY, H-ZSM-5, and MCM-41 Modified with Ga and Al