Abstract:Li-metal batteries have the potential to become the next generation of batteries since they can provide an increased energy density vs. Li-ion batteries. However, the safety issue caused by the inhomogeneous Li deposition and Li dendrite growth greatly limits their commercial application. Several methods have been proposed to address this issue. On the one hand, when Li ions are released from one electrode and consumed at the other electrode, it causes a salt concentration gradient. Besides, the electrical migration of anions in the opposite direction aggravates the concentration of gradient since anions do not react at the electrodes. Fast dendritic growth then occurs when the current is high enough to fully deplete the Li+ ion at the anode during charge. Thus, suppressing concentration gradient by immobilizing the anions would in principle solve the fast dendritic growth issue. On the other hand, the Solid Electrolyte Interphase (SEI) plays a crucial role in the operation of Li metal batteries since it prevents further reduction and continuous electrolyte reaction. SEI derives from the passivation layer formed onto the surface of Li metal under dry air during lithium foil extrusion and then evolves further in contact with the electrolytes and during subsequent electrochemical Li stripping/plating. The SEI is inhomogeneous and since it contains lower resistance pathways for Li+ transport, it favors inhomogeneous deposition at any current. Thus, SEI engineering, in order to favor the homogeneity of current density and enhanced mechanical properties to confine lithium could, in principle, improve the performance of Li metal batteries. Thus, we studied the use of single-ion conducting polymers with high cationic transference numbers (tLi + close to 1) as artificial SEIs (art-SEIs) since they include immobile anions and thus prevent Li+ depletion during charge and, at the same time, improve lithium metal confinement and the homogeneity of current density. Our results show much improved homogeneity of Li deposition and cycling stability after single-ion art-SEI coating using an ether-based liquid electrolyte combined with a separator. Nevertheless, it could not enable long-term cycling as the separator does not enable homogeneous pressure and current density onto the lithium anode. Thus, the use of a single-ion conducting solid polymer electrolyte was combined with a single-ion conducting art-SEI (as illustrated in Figure 1). This strategy allows the suppression of salt concentration gradients, inhomogeneous pressure and current density, thus enables homogeneous Li deposition and long-term cycling of Li metal anode. Figure 1

A polymeric artificial solid electrolyte interface dramatically enhances lithium-ion transport

A Bifunctional Composite Artificial Solid Electrolyte Interphase for High Stable Solid-State Lithium Batteries

A polythiourea protective layer for stable lithium metal anodes

Dynamic Interfacial Protection via Molecularly Tailored Copolymer for Durable Artificial Solid Electrolyte Interphase in Lithium Metal Batteries

Polymer–inorganic solid–electrolyte interphase for stable lithium metal batteries under lean electrolyte conditions

Material-electrolyte Interfacial Interaction Enabling the Formation of an Inorganic-Rich Solid Electrolyte Interphase for Fast-Charging Si-based Lithium-Ion Batteries

Interface Design Enabling Stable Polymer/Thiophosphate Electrolyte Separators for Dendrite-Free Lithium Metal Batteries.

In situ formation of polymer-inorganic solid-electrolyte interphase for stable polymeric solid-state lithium-metal batteries

Boron‐Doped Electrolytes as Interfacial Modifiers for High‐Rate Stable Lithium Metal Batteries

An Artificial Solid Electrolyte Interphase with High Li‐Ion Conductivity, Mechanical Strength, and Flexibility for Stable Lithium Metal Anodes

Poly(ethylene oxide)-based composite solid electrolyte for long cycle life solid-state lithium metal batteries: Improvement of interface stability through a dual mechanism

Artificial SEI Layer Combined with Single-Ion Polymer Electrolytes to Prevent Dendrite Growth in Lithium Metal Batteries

A bicomponent electrolyte additive towards stabilized interface for high-performance lithium-ion batteries

Stable artificial solid electrolyte interfaces for lithium batteries

Bi-containing Electrolyte Enables Robust and Li Ion Conductive Solid Electrolyte Interphase for Advanced Lithium Metal Anodes

Stabilization of Lithium Metal Interfaces by Constructing Composite Artificial Solid Electrolyte Interface with Mesoporous TiO2 and Perfluoropolymers

Constructing multifunctional solid electrolyte interface via in-situ polymerization for dendrite-free and low N/P ratio lithium metal batteries

Constructing Li‐Rich Artificial SEI Layer in Alloy–Polymer Composite Electrolyte to Achieve High Ionic Conductivity for All‐Solid‐State Lithium Metal Batteries

In-situ constructed polymer/alloy composite with high ionic conductivity as an artificial solid electrolyte interphase to stabilize lithium metal anode

Lithium Dendrite Suppression and Enhanced Interfacial Compatibility Enabled by an Ex Situ SEI on Li Anode for LAGP-Based All-Solid-State Batteries

A Dual Functional Artificial SEI Layer Based on a Facile Surface Chemistry for Stable Lithium Metal Anode