Abstract:The Co-Ni bimetal based catalysts had been considered as promising candidates for the CO2 reforming of CH4 reaction due to the Co-Ni synergistic effect. In order to further improve the catalytic property and anti-coke performance, Mg and Ca alkaline-promoted Co-Ni bimetal ordered mesoporous materials had been designed and fabricated by one-pot evaporation induced self-assembly method, which could be directly used as the catalysts for CRM reaction. These mesoporous catalysts were systematically characterized by XRD, N2 adsorption-desorption analysis, TEM, EDS, XPS, H2-TPR, and CO2-TPD. It was found that the materials calcined at 700°C could successfully maintain relatively large surface areas (120–212m2/g), big pore volumes (0.27–0.48cm3/g), and narrow pore size distribution (9.5–11.0nm), which could accommodate the gaseous feedstock with sufficient accessible Co-Ni active centers. Meanwhile, the Co-Ni active centers were in situ introduced into and confined by the ordered mesoporous framework by one-pot strategy, which could effectively inhibit the thermal agglomeration of Co-Ni nanoparticles. The presence of the Mg and Ca basic modifiers greatly intensified the surface basicity and enhanced the chemisorption of CO2, which would be beneficial to the activation of CO2 and the acceleration of the coke-elimination process. The present Co-Ni bimetal catalysts promoted by Mg and Ca displayed higher catalytic activities and better coke-resistant performance than the Co-Ni reference catalyst without any alkaline modification. Therefore, the present Mg and Ca alkaline elements promoted Co-Ni bimetal based ordered mesoporous catalysts promised potential candidates for CRM reaction.

Sensitivity of the properties and performance of Co catalyst to the nature of support for CO2 reforming of CH4

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Support composition effect on the structures, metallic sites formation, and performance of Ni-Co-Mg-Al-O composite for CO2 reforming of CH4

Effect of Modified Alumina Support on the Performance of Ni-Based Catalysts for CO2 Reforming of Methane

Study of Partial Oxidation and CO2 Reforming of Methane on Co Based Catalysts

Investigation of CH<sub>4</sub> Reforming with CO<sub>2</sub> on Meso-Porous Al<sub>2</sub>O<sub>3</sub>-Supported Ni Catalyst

Carbon Dioxide Reforming of Methane over Cobalt‐Nickel Bimetal‐Doped Ordered Mesoporous Alumina Catalysts with Advanced Catalytic Performances

Catalytic CO2 reforming of CH4 over MgAl2O4 supported Ni-Co catalysts for the syngas production

Investigation of CH 4 Reforming with CO 2 on Meso-Porous Al 2 O 3 -Supported Ni Catalyst

Supported Cobalt Catalyst Promoted by Noble Metals for CH4/CO2 Reforming to SyngasⅠ.Preparation Conditions and Performance of Pt-Co/Al2O3 Catalyst

Durable Ni/Mgo Catalysts For Co2 Reforming Of Methane: Activity And Metal-Support Interaction

Performance of supported nickel catalyst for reforming of CH 4 with CO 2 to syngas: I. Effect of preparation conditions and Ni loading

Meso-porous Ni/Mg/Al catalysts for methane reforming with CO2

Role of Support in CO2 Reforming of CH4 over a Ni/γ-Al2O3 Catalyst

Synergetic Effect Of Ni And Co In Ni-Co/Sba-15-Cd Catalysts And Their Catalytic Performance In Carbon Dioxide Reforming Of Methane

Performance of supported nickel catalyst for reforming of CH 4 with CO 2 to syngas: II . Effect of basic promoters

Alkaline-promoted Co-Ni Bimetal Ordered Mesoporous Catalysts with Enhanced Coke-Resistant Performance Toward CO 2 Reforming of CH 4

Tailored Ni-MgO Catalysts: Unveiling Temperature-Driven Synergy in CH4-CO2 Reforming

Supported Co Catalysts for Methane Reforming with CO2

Bound-state Ni species — a superior form in Ni-based catalyst for CH4/CO2 reforming

Insight and comprehensive study of Ni-based catalysts supported on various metal oxides for CO2 methanation